Controlled Hydrolytic Degradation of Polyglycolide–Caprolactone-Based Bioabsorbable Copolymer


Affiliations
1 Material Science Division, Shriram Institute for Industrial Research, 19-University Road, Delhi 110 007, India
 

Polyglycolide–caprolactone (PGCL)-based copolymer was synthesized from glycolide and caprolactone by ring opening polymerization in the presence of stannous octoate catalyst and diethylene glycol initiator. The effects of prepolymerization time, monomer ratio, monomer-to-catalyst and monomer-to-initiator ratios on per cent weight conversion were optimized. The end-capped copolymer was synthesized to make absorbable sutures having controlled bioabsorbability at different pH levels. It was observed that endcapped absorbable copolymer was more stable at pH 10.0 compared to uncapped absorbable material. End-capped copolymer also retained higher tensile strength compared to uncapped copolymer after 21 days. This phenomenon of controlled hydrolytic degradation of PGCL-based bioabsorbable polymer having terminal group end-capping can be attributed to less availability of hydrophilic end groups facilitating hydrolytic degradation of polymers.

Keywords

Biocompatibility, Bioabsorbable Copolymer, Hydrolytic Degradation, Polyglycolide–Caprolactone, Suture.
User
Notifications
Font Size

  • Gilding, D. K. and Reed, A. M., Biodegradable polymers for use in surgery – polyglycolic/poly(actic acid) homo- and copolymers: 1. Polymer, 1979, 20, 1459–1464.

  • Deasy, P. B., Finan, M. P. and Meegan, M. J., Synthesis and characterization of poly(D,L-lactide-co-glycolide) copolymer. J. Microencapsulation, 1989, 6(3), 369–378.

  • Chu, C. C. and Moncrief, G., An in vitro evaluation of the stability of mechanical properties of surgical suture materials in various pH conditions. Ann. Surg., 1983, 198(2), 223–228.

  • Chu, C. C., A comparison of the effect of pH on the biodegradation of two synthetic absorbable sutures. Ann. Surg., 1982, 195, 55–59.

  • Chu, C. C., Mechanical properties of suture materials: an important characterization. Ann. Surg., 1981, 193, 365–367.

  • Dawkins, J. V., Denyer, R. and Maddock, J. W., Molecular weights by gel permeation chromatography: unperturbed dimensions calibration for polyisoprene. Polymer, 1969, 10, 154–158.

  • Kim, C. W., Talac, R., Lu, L., Moore, M. J., Currier, B. L. and Yaszemski, M. J., Characterization of porous injectable poly(propylene fumarate)-based bone graft substitute. J. Biomed. Mater. Res. Part A, 2008, 85, 1114–1119.

  • Young, S. et al., Accelerating bone generation and bone mineralization in the interparietal sutures of rats using an rhBMP-2/ACS composite after rapid expansion. Tissue Eng. Part A, 2009, 15, 2347–2362.

  • Chellamani, K. P., Veerasubramanian, D. and Vignesh Balaji, R. S., Implantable medical textiles: synthetic suture manufacturing technology. J. Acad. Indust. Res., 2014, 3(2), 67–72.

  • Gupta, V. B. and Kothari, V. K., Manufactured Fibre Technology, Chapman and Hall, London, 1997, 1st edn, pp. 31–66.

  • Gogoi, R., Sarwar Alam, M. and Khandal, R. K., Effect of reaction time on the synthesis and properties of isocyanate terminated polyurethane prepolymer. Int. J. Eng. Res. Technol., 2014, 3(5), 1404–1411.

  • Haesslein, A. et al., Long-term release of fluocinolone acetonide using biodegradable fumarate-based polymers. J. Controlled Rel., 2006, 114, 251–260.

  • Ueda, H. et al., Injectable, in situ forming poly(propylene fumarate)based ocular drug delivery systems. J. Biomed. Mater. Res. Part A, 2007, 83, 656–666.

  • Hacker, M. C. et al., Effect of drying history on swelling properties and cell attachment to oligo(poly(ethylene glycol) fumarate) hydrogels for guided tissue regeneration applications. J. Biomed. Mater. Res. Part A, 2009, 88, 976–989.

  • Lee, K.-W., Wang, S., Yaszemski, M. J. and Lu, L., Physical properties and cellular responses to crosslinkable poly(propylene fumarate)/hydroxyapatite nanocomposites. Biomaterials, 2008, 29, 2839–2848.

  • Jayabalan, M., Shalumon, K. T., Mitha, M. K., Ganesan, K. and Epple, M., Acta effect of calcium precursors and pH on the precipitation of carbonated hydroxyapatite. Biomaterialia, 2010, 6, 763–775.

  • Lee, K.-W., Wang, S., Dadsetan, M., Yaszemski, M. J. and Lu, L., Enhanced cell in growth and proliferation through threedimensional nanocomposite scaffolds with controlled pore structures. Biomacromolecules, 2010, 11, 682–689.

  • Mistry, A. S., Mikos, A. G. and Jansen, J. A., Degradation and biocompatibility of a poly(propylene fumarate)-based/alumoxane nanocomposite for bone tissue engineering. J. Biomed. Mater. Res. Part A, 2007, 83, 940–953.

  • Mistry, A. S., Cheng, S. H., Yeh, T., Christenson, E., Jansen, J. A. and Mikos, A. G., Fabrication and in vitro degradation of porous fumarate-based polymer/alumoxane nanocomposite scaffolds for bone tissue engineering. J. Biomed. Mater. Res. Part A, 2009, 89, 68–79.

  • Mistry, A. S., Pham, Q. P., Schouten, C., Yeh, T., Christenson, E. M., Mikos, A. G. and Jansen, J. A., In vivo bone biocompatibility and degradation of porous fumarate-based polymer/alumoxane nanocomposites for bone tissue engineering. J. Biomed. Mater. Res. Part A, 2010, 92, 451–462.

  • Danti, S., D’Alessandro, D., Pietrabissa, A., Petrini, M. and Berrettini, S., Development of tissue-engineered substitutes of the ear ossicles: PORP-shaped poly(propylene fumarate)-based scaffolds cultured with human mesenchymal stromal cells. J. Biomed. Mater. Res. Part A, 2010, 92, 1343–1356.

  • Nguyen, C., Young, S., Kretlow, J. D., Mikos, A. G. and Wong, M. A., composite critical-size rabbit mandibular defect for evaluation of craniofacial tissue regeneration. J. Oral Maxillofacial Surg.. 2011, 69, 11–18.

  • Rosen, H. B., Chang, J., Wnek, G. E., Linhardt, R. J. and Langer, R., Bioerodible polyanhydrides for controlled drug delivery. Biomaterials, 1983, 4, 131–133.


Abstract Views: 321

PDF Views: 114




  • Controlled Hydrolytic Degradation of Polyglycolide–Caprolactone-Based Bioabsorbable Copolymer

Abstract Views: 321  |  PDF Views: 114

Authors

Anil Kumar Singh
Material Science Division, Shriram Institute for Industrial Research, 19-University Road, Delhi 110 007, India
Rakesh Kumar Singh
Material Science Division, Shriram Institute for Industrial Research, 19-University Road, Delhi 110 007, India
Ajay Kumar Tyagi
Material Science Division, Shriram Institute for Industrial Research, 19-University Road, Delhi 110 007, India

Abstract


Polyglycolide–caprolactone (PGCL)-based copolymer was synthesized from glycolide and caprolactone by ring opening polymerization in the presence of stannous octoate catalyst and diethylene glycol initiator. The effects of prepolymerization time, monomer ratio, monomer-to-catalyst and monomer-to-initiator ratios on per cent weight conversion were optimized. The end-capped copolymer was synthesized to make absorbable sutures having controlled bioabsorbability at different pH levels. It was observed that endcapped absorbable copolymer was more stable at pH 10.0 compared to uncapped absorbable material. End-capped copolymer also retained higher tensile strength compared to uncapped copolymer after 21 days. This phenomenon of controlled hydrolytic degradation of PGCL-based bioabsorbable polymer having terminal group end-capping can be attributed to less availability of hydrophilic end groups facilitating hydrolytic degradation of polymers.

Keywords


Biocompatibility, Bioabsorbable Copolymer, Hydrolytic Degradation, Polyglycolide–Caprolactone, Suture.

References





DOI: https://doi.org/10.18520/cs%2Fv113%2Fi07%2F1354-1360