Effect of Graphene Filler Content on Mechanical Strength and Hardness for Goat Hair Fibre Reinforced Epoxy Composites


Affiliations
1 Mech. Engg. Dept., Advanced Research Institute, Dr. MGR Educational and Research Institute University, Maduravoyal, Chennai, India
2 National Centre for Nano Science and Nano Tech., University of Madras, Guindy Campus, Chennai, India
 

   Subscribe/Renew Journal


Graphene when mixed in small quantity to host matrix like epoxy improves the mechanical, thermal and electrical properties. Fabrication of natural composite is made with goat hair as fibre with 37.5% fibre content by weight and graphene filled epoxy as matrix to enhance the properties. In the process of composite fabrication, five layers of goat hair fibre is sandwiched using resin by compression moulding method. Four composite specimens respectively epoxy with no Graphene content and 0.25% to 0.75% Graphene filled epoxy matrix are tested for tensile strength, flexural strength, impact strength and hardness. The mechanical properties of the four composite specimens are analysed. The experimental test results have demonstrated that graphene filled epoxy matrix reinforced with goat hair fibre specimens had better mechanical properties than composite with no graphene content.

Keywords

Goat Hair Fibre, Graphene, Epoxy Matrix, Nanomaterials, Mechanical Strength, Hardness.
User
Subscription Login to verify subscription
Notifications
Font Size

Abstract Views: 395

PDF Views: 192




  • Effect of Graphene Filler Content on Mechanical Strength and Hardness for Goat Hair Fibre Reinforced Epoxy Composites

Abstract Views: 395  |  PDF Views: 192

Authors

J. Jayaseelan
Mech. Engg. Dept., Advanced Research Institute, Dr. MGR Educational and Research Institute University, Maduravoyal, Chennai, India
P. Palanisamy
Mech. Engg. Dept., Advanced Research Institute, Dr. MGR Educational and Research Institute University, Maduravoyal, Chennai, India
K. R. Vijayakumar
Mech. Engg. Dept., Advanced Research Institute, Dr. MGR Educational and Research Institute University, Maduravoyal, Chennai, India
A. Dhanam Maria Vinita
National Centre for Nano Science and Nano Tech., University of Madras, Guindy Campus, Chennai, India

Abstract


Graphene when mixed in small quantity to host matrix like epoxy improves the mechanical, thermal and electrical properties. Fabrication of natural composite is made with goat hair as fibre with 37.5% fibre content by weight and graphene filled epoxy as matrix to enhance the properties. In the process of composite fabrication, five layers of goat hair fibre is sandwiched using resin by compression moulding method. Four composite specimens respectively epoxy with no Graphene content and 0.25% to 0.75% Graphene filled epoxy matrix are tested for tensile strength, flexural strength, impact strength and hardness. The mechanical properties of the four composite specimens are analysed. The experimental test results have demonstrated that graphene filled epoxy matrix reinforced with goat hair fibre specimens had better mechanical properties than composite with no graphene content.

Keywords


Goat Hair Fibre, Graphene, Epoxy Matrix, Nanomaterials, Mechanical Strength, Hardness.