Investigation of Heat Treatment on Mechanical Properties of Mild Steel


Affiliations
1 Dept. of MED, IET Bhaddal, Ropar, India
2 Dept. of MED, IET Bhaddal, Ropar, Punjab, India
 

Aim of this research paper is to investigate the effect of heat treatment on mechanical propertiesof Mild Steel (ASTM A36). Heat treatment was carried out in a furnace at a temperature of 800oC, after heating at such temperature quenching was carried out using brine solution. It was observed that on heating the mild steel resembles the properties of cast iron along with increase in boiling temperature.Various mechanical properties such as Tensile strength, yield strength, modulus of elasticity, bulk modulus, shear modulus, Poisson’s ratio, elongation percentage & hardness are analyzed to investigate the effect of heat treatment on the mild steel. To investigate the microstructure of the heat treated surface, grinding with the help of rough emery paper and by using alumina paste on double disk polishing machine was carried out. It was revealed that heat treatment produces significant effect on properties of Mild steel.

Keywords

Boiling Point, Brittle, Free From Rust, Alumina Paste, Emery Paper.
User
Notifications
Font Size

  • Adedayo A.V., Ibitoye S.A. &Oyetoyan O.A. (2010), “Annealing Heat Treatment Effects on Steel Welds”.Journal of Minerals & Materials Characterization & Engineering, 9(6), 547-557.

  • Bipin, K. S., Tewari, S. P. &Jyoti, P. (2010), “A Review on Effects of Preheating and/or Post Weld HeatTreatment (PWHT) on Mechanical Behavior of Ferrous Metals”. International Journal of Engineering Scienceand Technology, 2(4), 625-626.

  • David, Hart (1999). Welding and Coating Metallurgy 2. Published in Austalia, 6-7, 12.

  • Fadare, D. A., Fadara, T. G. &Akanbi, O. Y. (2011), “Effect of Heat Treatment on Mechanical Properties andMicrostructure of NST 37-2 Steel”. Journal of Minerals & Materials Characterization & Engineering, 10(.3),299-308.

  • International Institute of Welding Guidelines (1988). For the Classification of Ferrite Steel Weld Metal Microstructure Constituents Using the Light Microscopy: International Institute of Welding, IIW DOC. IX1533-88. Kahn Robert &Haasen Peter (1996). Physical Metallurgy. 4th Edition, Holland.

  • Rajan, T.V., Sharma C.P., & Sharma A. (1988). Heat Treatment Principles and Techniques. Prentice-Hall ofIndia, Private Ltd. New Delhi.

  • S.C.Rangwala, K.S. Rangwala& P.S. Rangwala, Engineering Materials (Material Science).

  • G.K.Narula, K.S. Narula, V.K.Gupta, Material science, Tata McGraw hill,.

  • V. Rajendran, Material science,Tata McGraw hill.


Abstract Views: 209

PDF Views: 0




  • Investigation of Heat Treatment on Mechanical Properties of Mild Steel

Abstract Views: 209  |  PDF Views: 0

Authors

Rajesh Jha
Dept. of MED, IET Bhaddal, Ropar, India
Siddharth Ranjan
Dept. of MED, IET Bhaddal, Ropar, India
Rakesh Kumar
Dept. of MED, IET Bhaddal, Ropar, India
Mithlesh Sharma
Dept. of MED, IET Bhaddal, Ropar, Punjab, India

Abstract


Aim of this research paper is to investigate the effect of heat treatment on mechanical propertiesof Mild Steel (ASTM A36). Heat treatment was carried out in a furnace at a temperature of 800oC, after heating at such temperature quenching was carried out using brine solution. It was observed that on heating the mild steel resembles the properties of cast iron along with increase in boiling temperature.Various mechanical properties such as Tensile strength, yield strength, modulus of elasticity, bulk modulus, shear modulus, Poisson’s ratio, elongation percentage & hardness are analyzed to investigate the effect of heat treatment on the mild steel. To investigate the microstructure of the heat treated surface, grinding with the help of rough emery paper and by using alumina paste on double disk polishing machine was carried out. It was revealed that heat treatment produces significant effect on properties of Mild steel.

Keywords


Boiling Point, Brittle, Free From Rust, Alumina Paste, Emery Paper.

References