Erosive Behaviour of HVOF Sprayed Coatings:A Review


Affiliations
1 Mechanical Engg. Department, IKGPTU, Kapurthala, 144603, India
2 Mechanical Engg., YCOE, PU Campus, 151302, India
 

Slurry erosion of turbine components in hydro power plants is a serious problem faced all over the world. Researchers are continuously working on investigating the ways to mitigate the effect of slurry erosion. Different techniques are employed to protect the material from deteoriation of its life, techniques such as filtration of the sand particles were carried out to reduce the amount of sand particles in the water which is impacting on the turbine components and designing the shape of turbine components in such a manner so as to mitigate the effect of slurry erosion. Still slurry erosion is most priortize area among the researchers as it is causing heavy economic losses. As a new alternative, researchers are exploring the thermal spray coating technique as an option by which the surface properties of the material will be improved. Thermal spraying is one of the most prominent methods used now a days to prevent the material from abrasive wear, high temperature corrosion, erosive wear and stresses, as it increases the life span of material used in service. High velocity Oxy Fuel (HVOF) spraying is among the thermal spraying techniques which are known for its various characteristics such as providing hardness, wear resistant and dense micro structured coatings. In this paper an attempt has been made to present a state of art review of the work done by various researchers to prevent slurry erosion of hydraulic machine components by using HVOF Spray technique.

Keywords

Thermal Spraying, HVOF, Erosion.
User
Notifications
Font Size

  • Bajracharya T R, Joshi C B, Saini R P, Dahlhaug O G, Wear, 264 (2008),177–184.

  • Chawla V, Sidhu B S, Puri D and Singh P, Journal of the Australian Ceramic Society, 44 (2008), 56-62.

  • Sidhu B S, Puri D, Prakash S, Journal of Materials Processing Technology, 159 (2005), 347–355.

  • Goyal R, Buta S S, Grewal J S,International Journal of Engineering Studies, 3 (2010), 351-357.

  • Federici M , Cinzia M , Moscatelli A, Gialanella S , Straffelini G, Wear, 368-369 (2016), 326–334.

  • Santa J.F., Espitia L A, Blanco J A, Romo S A, Toro A, Wear, 267 (2007), 160–167.

  • Abd-Elrhman Y M., Abouel-Kasem A, Emara K M, Journal of Engineering Sciences, Assiut University, 41 (2013), 137-157.

  • Jha A K, Batham R, Ahmed M, Majumder A K., Modi O P, Chaturvedi S, Gupta A K,Trans. Nonferrous Met. Soc. China, 21 (2011), 32−38.

  • Energy fact book 2015-2016, Tech. Rep., Natural Resources Canada, available at : ( HTTP// www.nccan.gc.ca/energy/), 2016.

  • Gupta R, Singh S N, Seshadri V, Accelerated wear rate test rig for the predicting of erosion in slurry pipelines, in: 19th NCFMFP, IIT, Bombay, 1992, pp. C1-1-C1-4.

  • Bitter J G A, Wear, 6 (1) (1963), 5-21.

  • Desale G R, Gandhi B K, Jain S C, Wear 259 (2005), 196-202.

  • Schematic view of HVOF process”,www.gordonengland.co.uk

  • Peat T, Gallowa A, Toumpis A, Harvey D, Yang W H, Surface & Coatings Technology, 300 (2016),118–127.

  • Taillon G, Pougoum F, Lavigne S, Laurent T, Schulz R , Bousser E, Savoie S , Martinu L, Wear, 364-365 (2016),201–210.

  • Thakur L, Arora N, Surf. Coat.Technol., 25(2016).

  • Goyal D K, Singh H, Kumar H and Sahni V, Journal of thermal spray technology, 21(2012),838-851.

  • Goyal D K, Singh H, Kumar H and Sahni V, Journal of Tribology,136 (2014), 0416021-0416032.

  • Vashishtha N, Khatirkar R K, Sapate S G , Tribology International, 105 (2017),55–68.

  • Kumar A, Sharma A, Goel S K, Applied Surface Science 370 (2016),418–426.

  • Hawthorne H M, Arsenault B, Immarigeon J P, Legoux J G, Parameswaran V R, Wear, 225–229(1999),825–834.

  • Hong S, Wu Y , Zhang J, Zheng Y, Lin J, Ultrasonics Sonochemistry, 31 (2016), 563–569.

  • Praveena A S , Sarangana J, Suresha S, Channabasappa B H, Ceramics International, 42 (2016),1094–1104.

  • Peat T , Alexander M G, Athanasios I T, Harvey D, Surface & Coatings Technology, 299 (2016), 37–48.

  • Wanga Q, Wu X, Li L, Zhigang L, Lin S, Procedia Engineering, 27 (2012),1758 – 1765.

  • Ciubotariu C R, Frunzaverde D, Marginean G, Șerban V A, Birdeanu A V, Optics & Laser Technology, 77 (2016), 98–103.

  • Bolelli G, Berger L M, Borner T, Koivuluoto H, Matikainen V, Lusvarghi L, Lyphout C, Markocsan N, Nylen P, Sassatelli P, Trache R, Vuoristo P, Wear, 358-359 (2016), 32–50.

  • Ramesh M R, . Prakash S, Nath S K, Sapra P K, Venkataraman B, Wear,269 (2010),197–205.

  • Yuan J, Chunwei M, Yang S, Yu Z, Hua L, Surface & Coatings Technology,285 (2016), 17–23.

  • Hong S, Yuping W , Wang Q, Ying G, Li G, Gao W, Wang B, Wenmin G, Surface & Coatings Technology, 225 (2013), 85–91.

  • Wang Y., Zheng Y G,. Ke W, Sun H, Hou W L, Chang X C, Wang J Q, Corrosion Science, 53 (2011), 3177–3185.

  • Zhang-xiong D, Wei C, Qun W, Trans. Nonferrous Met. Soc. China, 21(2011), 2231−2236.

  • Mann B S, Arya V, Maiti A K, Rao M U B., Joshi P, Wear,60 (2006), 75–82.

  • Wu Y, Hong S, Zhang J, Zhihua H, Wenmin G, Wang Q, Li G, Int. Journal of Refractory Metals and Hard Materials,32 (2012), 21–26.

  • Ramesh M R, Prakash S, Nath S K, Sapra P K, Wear, 269 (2010), 197–205.

  • Thakur L, Arora N, Wear, 303 (2013), 405–411.

  • Liu W H, Shieu F S, Hsia W T, Surface & Coatings Technology ,249 (2014), 24–41.

  • Mahdipoor M S, Tarasi F, Moreau C, Dolatabadi A, Medra M, Wear 330-331 (2015), 338–347.

  • Gariboldi E, Rovatti L, Lecis N, Mondora L, Mondora G A, Surface and Coatings Technology, 305 (2016), 268-274.


Abstract Views: 155

PDF Views: 0




  • Erosive Behaviour of HVOF Sprayed Coatings:A Review

Abstract Views: 155  |  PDF Views: 0

Authors

Mithlesh Sharma
Mechanical Engg. Department, IKGPTU, Kapurthala, 144603, India
Deepak Kumar Goyal
Mechanical Engg. Department, IKGPTU, Kapurthala, 144603, India
Gagandeep Kaushal
Mechanical Engg., YCOE, PU Campus, 151302, India

Abstract


Slurry erosion of turbine components in hydro power plants is a serious problem faced all over the world. Researchers are continuously working on investigating the ways to mitigate the effect of slurry erosion. Different techniques are employed to protect the material from deteoriation of its life, techniques such as filtration of the sand particles were carried out to reduce the amount of sand particles in the water which is impacting on the turbine components and designing the shape of turbine components in such a manner so as to mitigate the effect of slurry erosion. Still slurry erosion is most priortize area among the researchers as it is causing heavy economic losses. As a new alternative, researchers are exploring the thermal spray coating technique as an option by which the surface properties of the material will be improved. Thermal spraying is one of the most prominent methods used now a days to prevent the material from abrasive wear, high temperature corrosion, erosive wear and stresses, as it increases the life span of material used in service. High velocity Oxy Fuel (HVOF) spraying is among the thermal spraying techniques which are known for its various characteristics such as providing hardness, wear resistant and dense micro structured coatings. In this paper an attempt has been made to present a state of art review of the work done by various researchers to prevent slurry erosion of hydraulic machine components by using HVOF Spray technique.

Keywords


Thermal Spraying, HVOF, Erosion.

References