Indian Journal of Engineering & Materials Sciences

Open Access Open Access  Restricted Access Subscription Access

Mechanical properties and kinetics of boride layers on AISI D2 steel produced by plasma paste boriding


Affiliations
1 Laboratory of Materials Technology, Faculty of Mechanical Engineering and Process Engineering, USTHB, B.P. No. 32, 16111 El-Alia, Bab-Ezzouar, Algiers,, Algeria
2 Poznan University of Technology, Institute of Materials Science and Engineering, Pl. M Sklodowskiej-Curie 5, 60-965 Poznan, Poland

In the present study, the AISI D2 steel has been treated by the plasma paste boriding process using a gas mixture of 70% H2-30% Ar with 70% of borax and 30% SiC. The boriding treatment has been carried out at 700, 750 and 800 °C for an exposure time of 3 to 7 h. The plasma paste borided samples have been investigated by various techniques such as scanning electron microscopy, optical microscopy, XRD analysis, micro-hardness Vickers and the rockwell-C adhesion tests. The fracture toughness has also been measured on the plasma paste borided samples under different values of indentation load. From a kinetic point of view, the boride layers have obeyed the parabolic growth law. The value of boron activation energy for AISI D2 steel has been estimated as 130 kJ mol–1 using our experimental results. In addition, this obtained activation energy has been compared to the literature data.
User
Notifications
Font Size

Abstract Views: 90




  • Mechanical properties and kinetics of boride layers on AISI D2 steel produced by plasma paste boriding

Abstract Views: 90  | 

Authors

Mourad Keddam
Laboratory of Materials Technology, Faculty of Mechanical Engineering and Process Engineering, USTHB, B.P. No. 32, 16111 El-Alia, Bab-Ezzouar, Algiers,, Algeria
Natalia Makuch
Poznan University of Technology, Institute of Materials Science and Engineering, Pl. M Sklodowskiej-Curie 5, 60-965 Poznan, Poland
Michal Kulka
Poznan University of Technology, Institute of Materials Science and Engineering, Pl. M Sklodowskiej-Curie 5, 60-965 Poznan, Poland
Andrzej Miklaszewski
Poznan University of Technology, Institute of Materials Science and Engineering, Pl. M Sklodowskiej-Curie 5, 60-965 Poznan, Poland

Abstract


In the present study, the AISI D2 steel has been treated by the plasma paste boriding process using a gas mixture of 70% H2-30% Ar with 70% of borax and 30% SiC. The boriding treatment has been carried out at 700, 750 and 800 °C for an exposure time of 3 to 7 h. The plasma paste borided samples have been investigated by various techniques such as scanning electron microscopy, optical microscopy, XRD analysis, micro-hardness Vickers and the rockwell-C adhesion tests. The fracture toughness has also been measured on the plasma paste borided samples under different values of indentation load. From a kinetic point of view, the boride layers have obeyed the parabolic growth law. The value of boron activation energy for AISI D2 steel has been estimated as 130 kJ mol–1 using our experimental results. In addition, this obtained activation energy has been compared to the literature data.