Indian Journal of Pure and Applied Physics

Open Access Open Access  Restricted Access Subscription Access

Impedance and Electric Modulus Spectroscopy of Polycrystalline La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d Cathode Ceramic for Intermediate Temperature SOFCs


Affiliations
1 Department of Physics, Hindu college Moradabad, Moradabad, India-244 001, India
2 Department of Physics, Deen Dayal Upadhyaya Gorakhpur University, Gorakhpur, India-273 009, India

In the present research work, La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d cathode ceramic powder is synthesized through cost-effective flash pyrolysis process and further conventional heat treatment for sintering for IT-SOFCs. The crystal structure, unit cell parameters and bond length are determined by using the Rietveld refinement program. The XRD result indicates existence of a pure single phase with R C space group symmetry detected from the sample which has been sintered at 700 ℃. SEM images of fracture surface of sample sintered at 700 ℃ showed a high porosity and nano grain sizes (50-100 nm). Impedance and electric modulus spectroscopic methods are used to identify the relaxation phenomena in La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d ceramic over a broad range of temperature and frequency. A single relaxation peak is observed in the imaginary part of impedance and electric modulus spectra, which could be due to the contribution of grain boundary of La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d ceramic. The imaginary part of modulus ( ) spectra is analyzed with help of non-exponential decay function or Kohlrausch–Williams–Watts (KWW) parameter (β). In the combined plot of the imaginary part of impedance and electric modulus spectra at 210 ℃, only a single peak of and is observed at the same frequency which indicates that the conduction process is a long-range motion of the charge carriers. The frequency-dependent conductivity is followed by the Jonscher’s double power law in the temperature range 30-210 ℃.
User
Notifications
Font Size

Abstract Views: 99




  • Impedance and Electric Modulus Spectroscopy of Polycrystalline La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d Cathode Ceramic for Intermediate Temperature SOFCs

Abstract Views: 99  | 

Authors

Sunder Singh
Department of Physics, Hindu college Moradabad, Moradabad, India-244 001, India
Manindra Kumar
Department of Physics, Deen Dayal Upadhyaya Gorakhpur University, Gorakhpur, India-273 009, India
Anil Kumar
Department of Physics, Hindu college Moradabad, Moradabad, India-244 001, India
Deepash Shekhar Saini
Department of Physics, Deen Dayal Upadhyaya Gorakhpur University, Gorakhpur, India-273 009, India

Abstract


In the present research work, La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d cathode ceramic powder is synthesized through cost-effective flash pyrolysis process and further conventional heat treatment for sintering for IT-SOFCs. The crystal structure, unit cell parameters and bond length are determined by using the Rietveld refinement program. The XRD result indicates existence of a pure single phase with R C space group symmetry detected from the sample which has been sintered at 700 ℃. SEM images of fracture surface of sample sintered at 700 ℃ showed a high porosity and nano grain sizes (50-100 nm). Impedance and electric modulus spectroscopic methods are used to identify the relaxation phenomena in La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d ceramic over a broad range of temperature and frequency. A single relaxation peak is observed in the imaginary part of impedance and electric modulus spectra, which could be due to the contribution of grain boundary of La0.5Sr0.5Bi0.2Co0.4Fe0.4O3–d ceramic. The imaginary part of modulus ( ) spectra is analyzed with help of non-exponential decay function or Kohlrausch–Williams–Watts (KWW) parameter (β). In the combined plot of the imaginary part of impedance and electric modulus spectra at 210 ℃, only a single peak of and is observed at the same frequency which indicates that the conduction process is a long-range motion of the charge carriers. The frequency-dependent conductivity is followed by the Jonscher’s double power law in the temperature range 30-210 ℃.