Investigation of Optical Properties of Nanostructured Ce0.80-x-yNdxTby,/sub>O2 Compound


Affiliations
1 Department of Energy System Engineering, Kahramanmaraş İstiklal University, Kahramanmaraş, 46300, Turkey
2 Institute of Science, Material Science and Engineering, Kahramanmaraş Sütçü İmam University Kahramanmaraş, 46050, Turkey
3 Department of Metallurgical and Materials Engineering, Karamanoglu Mehmetbey University Karaman, Turkey
4 Department of Chemistry Processing Technologies, Kayseri University, Kayseri, Turkey
 

In this study, the sol-gel method synthesized nano-structured Ce0.80-x-yNdxTbyO2 compounds that can be used in optoelectronic devices. In the characterization studies of the synthesized compounds, XRD, FE-SEM-EDX, TG-DTA, Raman, and photoluminescence spectrophotometer were used. The thermal analysis determined that the degrading species were removed at 600 °C and cubic crystalline compounds were obtained according to the XRD data. EDX data confirmed the presence of host and activator elements in the compound. It was determined that oxygen vacancy formation was more intense in the 5% Nd-15%Tb doped compound. According to these results, 5% Nd phosphorus-doped Ce0.80-x-yNdxTbyO2 was reported to be a good candidate for optoelectronic applications where both red and green photoluminescence are required in the same crystal.

Keywords

CeO2, Optoelectronic, Sol-Gel.
User
Notifications
Font Size

  • Bakir A H & Torun H Ö, J Chem Soc Pak, 43 (2021).

  • Malleshappa J, Nagabhushana H, Prasad B D, Sharma S C, Vidya Y S & Anantharaju K S, Optik, 127 (2016) 855.

  • Fauzi A A, Jalil A A, Hassan N S, Aziz F F A, Azami M S, Hussain I & Vo D V, Chemosphere, 286 (2022)131651.

  • Yan S, Liang X, Song H, Ma S & Lu Y, Ceram Int, 44 (2018)358.

  • Masalov A, Viagin O, Maksimchuk P, Seminko V, Bespalova I, Aslanov A & Zorenko Y, J Lumin, 145 (2014) 61.

  • Cabello-Guzmán G, Fernandez L, Caro-Díaz C, Lillo L, Valenzuela-Melgarejo F, Seguel M & Buono-Core G E, Optik, 248 (2021) 168071.

  • Kunimi S & Fujihara S, ECS J Solid State Sci Technol, 1 (2012) R32.

  • Fujihara S & Oikawa M, J Appl Phys, 95 (2004) 8002.

  • Yoshida Y & Fujihara S, Eur J Inorg Chem, (2011).

  • Singh V, Rathaiah M, Venkatramu V, Haase M & Kim S H, Spectr Chimica Acta Part A: Mol Biomol Spectr, 122 (2014) 704.

  • Balestrieri M, Colis S, Gallart M, Schmerber G, Ziegler M, Gilliot P & Dinia A, J Mater Chem C, 3 (2015) 7014.

  • Choudhury B & Choudhury A, Curr Appl Phys, 13 (2013) 217.

  • Öztürk E & Ozpozan K N, J Therm Anal Calorim, 117 (2014) 573.

  • Öztürk E & Sarılmaz E, Mater Res Express, 6 (2019) 105710.

  • Uzun E, Öztürk E & Ozpozan K N, Luminescence, 33 (2018) 1346.

  • Wang Z, Quan Z & Lin J, Inorg Chem, 46 (2007) 5237.

  • Malleshappa J, Nagabhushana H, Sharma S C, Sunitha D V, Dhananjaya N, Shivakumara C & Nagabhushana B M, J Alloys Compd, 590 (2014) 131.

  • Malleshappa J, Nagabhushana H, Prasad B D, Sharma S C, Vidya Y S & Anantharaju K S. Structural, Optik, 127 (2016) 855.

  • Shannon R D, Acta Crystallog, 25 (1969) 925.

  • Jamshidijam M, Thangaraj P, Akbari-Fakhrabadi A, Galeano M A N, Usuba J & Viswanathan M R, Ceram Int, 43 (2017) 5216.

  • Keramidas V G & White W B, The J Chem Phys, 59 (1973) 1561.

  • Hernández W Y, Laguna O H, Centeno M A & Odriozola J A, J Solid State Chem, 184 (2011) 3014.

  • He D, Hao H, Chen D, Liu J, Yu J, Lu J & Luo Y, Catal Today, 281 (2017) 559.

  • Öztürk E & Sarılmaz E, Mater Chem Phys, 239 (2020) 122085.

  • Öztürk E, Ozpozan K N & Uzun E, J Chin Chem Soc, 62 (2015) 47.

  • Ding L, Zhanga Q, Luo J, Liua W, Zhou W & Yin S, J Alloys Compd, 509 (2011) 100167.

  • Singh V, Shinde K N, Pathak M S, Singh N, Dubey V, Singh Pramod K & Jirimali H D, Optik, 164 (2018) 407.

  • Kostyukov A I, Zhuzhgov A V, Kaichev V V, Rastorguev A A, Snytnikov V N & Snytnikov V N, Opt Mater, 75 (2018) 757.

  • Kim Y & Kang S, Acta Materialia, 59 (2011) 3024.


Abstract Views: 78

PDF Views: 50




  • Investigation of Optical Properties of Nanostructured Ce0.80-x-yNdxTby,/sub>O2 Compound

Abstract Views: 78  |  PDF Views: 50

Authors

Handan Ozlu Torun
Department of Energy System Engineering, Kahramanmaraş İstiklal University, Kahramanmaraş, 46300, Turkey
Rabia Kırkgecit
Institute of Science, Material Science and Engineering, Kahramanmaraş Sütçü İmam University Kahramanmaraş, 46050, Turkey
Esra Ozturk
Department of Metallurgical and Materials Engineering, Karamanoglu Mehmetbey University Karaman, Turkey
Fatma Kılıc Dokan
Department of Chemistry Processing Technologies, Kayseri University, Kayseri, Turkey

Abstract


In this study, the sol-gel method synthesized nano-structured Ce0.80-x-yNdxTbyO2 compounds that can be used in optoelectronic devices. In the characterization studies of the synthesized compounds, XRD, FE-SEM-EDX, TG-DTA, Raman, and photoluminescence spectrophotometer were used. The thermal analysis determined that the degrading species were removed at 600 °C and cubic crystalline compounds were obtained according to the XRD data. EDX data confirmed the presence of host and activator elements in the compound. It was determined that oxygen vacancy formation was more intense in the 5% Nd-15%Tb doped compound. According to these results, 5% Nd phosphorus-doped Ce0.80-x-yNdxTbyO2 was reported to be a good candidate for optoelectronic applications where both red and green photoluminescence are required in the same crystal.

Keywords


CeO2, Optoelectronic, Sol-Gel.