Dielectric Study of Ytterbium Doped ZnFe2O4 Spinel Ferrite Synthesized by Solution Combustion Method


Affiliations
1 Department of Physics, National Institute of Technology, Raipur 492 010, India
 

A series of ZnFe2O4 spinel ferrite doped with Ytterbium ions were synthesized using the solution combustion method. The XRD patterns of the prepared samples confirmed the cubic spinel structure with space group Fd-3m. Scherrer’s formula was used to calculate the crystallite size of the samples and it was found to be 20.69, 17.16 and11.09 nm. The SEM image showed irregular morphological distribution. The Dielectric constant and dielectric loss were studied at different temperatures and frequencies. The impedance analysis indicates that the conduction mechanism depends highly on the grain boundary resistance.

Keywords

Spinel ferrite; Dielectric constant; Dielectric loss; Impedance analysis.
User
Notifications
Font Size

  • Qindeel R, Alonizan N H, Alghamdi E A & Awad M A, J Sol-Gel Sci Technol, 97 (2021) 593.

  • Thakur P,Taneja S, Chahar D, Ravelo B & Thakur A, J Magn Magn Mater, 530 (2021) 167925.

  • Ehrhardt H,Campbell S J & Hofmann M, J Alloys Compd, 339 (2002) 225.

  • Ravinder D, Reddy A V R & Mohan G R, Mater Lett, 52 (2002) 259.

  • Vinosha P A, Mely L A, Jeronsia J E, Krishnan S & Das S J, Optik, 134 (2017) 99.

  • Zhang Y, Chen Y, Kou Q, Wang Z, Han D, Sun Y, Yang J, Liu Y & Yang L, J Mater Sci: Mater Electron, 29 (2018) 3665.

  • Heiba Z K, Mohamed M B, Ahmed M A, Moussa M A A & Hamdeh H H, J Alloys Compd, 586 (2014) 773.

  • Soudani I, Brahim K B B,Oueslati A, Aydi A, Khirouni K, Benali A, Dhahri E & Valente M A, RSC Adv, 13 (2023) 9260.

  • Mohapatra P P, Pittal S & Dobbidi P, J Mater Res Technol, 9 (2020) 2992.

  • Batoo K M, Mir F A, El-sadek M S A, Shahabuddin M & Ahmed N, J Nanoparticle Res, 15 (2013).

  • Hafiza M N & Isa M I N, Res J Recent Sci Res J Recent Sci, 3 (2014) 50.


Abstract Views: 84

PDF Views: 47




  • Dielectric Study of Ytterbium Doped ZnFe2O4 Spinel Ferrite Synthesized by Solution Combustion Method

Abstract Views: 84  |  PDF Views: 47

Authors

Laxmikant Banaj
Department of Physics, National Institute of Technology, Raipur 492 010, India
Sadhana Agrawal
Department of Physics, National Institute of Technology, Raipur 492 010, India

Abstract


A series of ZnFe2O4 spinel ferrite doped with Ytterbium ions were synthesized using the solution combustion method. The XRD patterns of the prepared samples confirmed the cubic spinel structure with space group Fd-3m. Scherrer’s formula was used to calculate the crystallite size of the samples and it was found to be 20.69, 17.16 and11.09 nm. The SEM image showed irregular morphological distribution. The Dielectric constant and dielectric loss were studied at different temperatures and frequencies. The impedance analysis indicates that the conduction mechanism depends highly on the grain boundary resistance.

Keywords


Spinel ferrite; Dielectric constant; Dielectric loss; Impedance analysis.

References