Characterization of Post FR Treatedtextile Materials:A Comparative Study


Affiliations
1 Department of Textile and Apparel Designing, College of Rural Home Science, University of Agricultural Sciences, Dharwad (Karnataka), India
2 Department of Textile and Apparel Designing, College of Rural Home Science, University of Agricultural Sciences, DHARWAD (KARNATAKA), India
     

   Subscribe/Renew Journal


Cotton and polyester fabrics were subjected to Atmospheric Pressure Plasma (APP) followed by Flame Retardant (FR) treatment using dielectric barrier discharge plasma with He-O2 gas mixture by padding mangle; dried and cured on hot air stenter. The main aim of the study was to assess the effect of plasma-FR treatment on fibre topography, structural and functional properties.Surface topography of treated test samples assessed under SEM and revealed about surface erosion of both the fibres through pictorial presentation. Positive enhancement not only in structural properties of FR finished fabrics viz., cloth count, thickness, GSM and dimensional stability but also the flame retardancy of cotton and polyester were noticed. Further, the qualitative improvements induced due to plasma-FR treatment were found to be sustainable on multiple washes. Thus, it is concluded that APP as a pre-treatment increases the fixation of FR agent into the etched fibre surface and induces sustainability of finish at greater levels.

Keywords

Cotton, Flame Retardant (FR), Helium-Oxygen Plasma Treatment, Polyester, Surface Topography.
Subscription Login to verify subscription
User
Notifications
Font Size


  • Bhat, N.V., Netravali, A.N., Gore, A.V., Sathianarayanan, M.P., Arolkar, G.A. and Deshmukh, R.R. (2011). Surface modification of cotton fabrics using plasma technology. Text. Res. J., 10(6): 1-13.

  • Kan, C.W., Lam, Y.L., Yuen, C.W.M. and Chen, K.S. (2011). Using plasma treatment for enhancing conventional flame-retardant finishing of cotton fabric. J. Appl. Polym. Sci., 102(6): 5958-5961.

  • Kaplan, S. (2004). Plasma processes for wide fabric, film and non-wovens. Surf. Coatings Tech., 186 : 214-217.

  • Lam, Y.L. Kan, C.W. and Yuen, C.W. (2011). Effect of oxygen plasma pretreatment and titanium dioxide overlay coating on flame retardant finished cotton fabrics. Bio-Resources, 6(2): 1454-1474.

  • Siriviriyanun, A., O’Rear, E.A. and Yanumet, N. (2008). Self-extinguishing cotton fabric with minimal phosphorus deposition. Cellulose, 15(5): 731-737.

  • Sparavigna, A. (2008). Plasma treatment advantages for textiles. ARXIV .org., 6(2): 1-16.

  • Wakelyn, P.J., Adair, P.K. and Barker, R.H. (2004). Do open flame ignition resistance treatments for cellulosic and cellulosic blend fabrics also reduce cigarette ignitions. Fire & Materials, 29(1): 15-26.


Abstract Views: 230

PDF Views: 0




  • Characterization of Post FR Treatedtextile Materials:A Comparative Study

Abstract Views: 230  |  PDF Views: 0

Authors

Archana Bahuguna
Department of Textile and Apparel Designing, College of Rural Home Science, University of Agricultural Sciences, Dharwad (Karnataka), India
Shailaja D. Naik
Department of Textile and Apparel Designing, College of Rural Home Science, University of Agricultural Sciences, DHARWAD (KARNATAKA), India

Abstract


Cotton and polyester fabrics were subjected to Atmospheric Pressure Plasma (APP) followed by Flame Retardant (FR) treatment using dielectric barrier discharge plasma with He-O2 gas mixture by padding mangle; dried and cured on hot air stenter. The main aim of the study was to assess the effect of plasma-FR treatment on fibre topography, structural and functional properties.Surface topography of treated test samples assessed under SEM and revealed about surface erosion of both the fibres through pictorial presentation. Positive enhancement not only in structural properties of FR finished fabrics viz., cloth count, thickness, GSM and dimensional stability but also the flame retardancy of cotton and polyester were noticed. Further, the qualitative improvements induced due to plasma-FR treatment were found to be sustainable on multiple washes. Thus, it is concluded that APP as a pre-treatment increases the fixation of FR agent into the etched fibre surface and induces sustainability of finish at greater levels.

Keywords


Cotton, Flame Retardant (FR), Helium-Oxygen Plasma Treatment, Polyester, Surface Topography.