Immersion Plating of Tin on Aluminium by Microwave Irradiation in Acidic Medium


Affiliations
1 Department of Chemistry, Government Arts College, Salem-636 007, Tamil Nadu, India
2 Department of Chemistry, Periyar University, Salem-636 011, Tamil Nadu, India
3 School of Display and Chemical Engineering, Yeungnam University, Gyeongsan, Korea, Republic of
     

   Subscribe/Renew Journal


Immersion tin coatings were formed directly on aluminium by microwave irradiation from acidic tin chloride bath. The corrosion resistance behaviour of the coatings was studied by Tafel polarization and EIS. The effects of bath composition, temperature and irradiation time on the kinetics of immersion plating of tin onto aluminium were investigated. The surface morphology of the coatings has been analyzed by SEM. The phase composition of the coatings was analyzed by X-Ray Diffraction. The deposit structure is found to be more crystalline. It is found that the deposited tin is dissolved again after a long time immersion in plating solution.

Keywords

Aluminium, Tin Immersion Plating, Corrosion Resistance and X-Ray Diffraction.
Subscription Login to verify subscription
User
Notifications
Font Size


Abstract Views: 251

PDF Views: 0




  • Immersion Plating of Tin on Aluminium by Microwave Irradiation in Acidic Medium

Abstract Views: 251  |  PDF Views: 0

Authors

M. Sherin Banu
Department of Chemistry, Government Arts College, Salem-636 007, Tamil Nadu, India
V. Raj
Department of Chemistry, Periyar University, Salem-636 011, Tamil Nadu, India
M. Mubarak Ali
School of Display and Chemical Engineering, Yeungnam University, Gyeongsan, Korea, Republic of

Abstract


Immersion tin coatings were formed directly on aluminium by microwave irradiation from acidic tin chloride bath. The corrosion resistance behaviour of the coatings was studied by Tafel polarization and EIS. The effects of bath composition, temperature and irradiation time on the kinetics of immersion plating of tin onto aluminium were investigated. The surface morphology of the coatings has been analyzed by SEM. The phase composition of the coatings was analyzed by X-Ray Diffraction. The deposit structure is found to be more crystalline. It is found that the deposited tin is dissolved again after a long time immersion in plating solution.

Keywords


Aluminium, Tin Immersion Plating, Corrosion Resistance and X-Ray Diffraction.