Effect of Sandblasting, Annealing and Hydrophobic Treatment on the Nano-Mechanical and Corrosion Behaviour of n-TiO2-Coated 316L Stainless Steel


Affiliations
1 Department of Chemical Engineering, COMSATS Institute of Information Technology, Lahore, Pakistan
2 King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia
 

In this article, the effect of hydrophobic coated and uncoated surfaces on the corrosion resistance, tribological property, and surface morphology and nanomechanical properties is presented. A hierarchical surface (micro/nano) was prepared by ultra shot penning of 316L stainless steel at 20 kHz. Chemical vapour deposition technique was used for deposition of the coating, and coating thickness of 0.5 μm was obtained. A maximum hardness of 6.7 and 6.32 GPa was exhibited by the sandblasted (SB), annealed (SBAT) and coated (SBAT) samples respectively. The beneficial effect of annealing and surface roughness was clearly indicated by the sandblasted, annealed and coated specimens. They showed the highest value of reduced modulus maximum resistance to scratch tests and a high adhesion as indicated by scratch path profiles. The lowest corrosion rates were obtained by SBAT specimens (1.32 mpy) in 3.5 wt% NaCl. After application of 3.5% fluoroalkylsilane (FAS13), the corrosion rate was reduced to 0.04 mpy with no evidence of localized pitting. The water contact angle using DSA-100 system was measured to be 120° for SBAT and 80-90° for the samples.

Keywords

Annealing, Chemical Vapour Deposition, Corrosion, Sandblasting, Super Hydrophobicity.
User
Notifications
Font Size

  • Barthlott, W. and Neinhuis, C., Purity of the sacred lotus, or escape from contamination in biological surfaces. Planta, 1997, 202, 1–8.

  • Von Bayer, H. C., The lotus-effect. Science, 2000, 40, 12–15.

  • Valipour, M. N, F. Ch. Birjandi and Sargolzaei, J., Super-nonwettable surfaces: a review. Colloids Surf., 2014, 448, 93–106.

  • Öner, D. and McCarthy, T. J., Ultra hydrophobic surfaces, effects of topography length scales on Wettability. Langmuir, 2000, 16, 7777–7782.

  • Callies, M. and Quere, D., On water repellency. Soft Mater, 2005, 1, 55–65.

  • Xi, Z., Shi, F., Niu, J., Jiaung, Y. and Wang, Z., Superhydrophobic surface from structural to functional applications. J. Mater. Chem., 2008, 18, 621–623.

  • Mahaduk Satish, A. et al., Thermally stable and transparent super hydrophobic sol–gel coatings by spray methods. J. Sol–Gel Sci. Technol., 2012, 63, 580–586.

  • Shen G. X., Chen, Y. C., Lin, L., Lin, C. J. and Scantlebnry, D., Study on hydrophobic Nano-TiO2 coating and its properties for corrosion protection, metals. Electro-chemical. Acta, 2005, 50, 5083–5089.

  • Ahmad, M. M., Hashim, M. A., Nabi, F., Ahmad, S. and Thabian, A., Anti-corrosion ability of surfactants, a review. Int. J. Electrochem.Sci., 2011, 8, 1927–1948.

  • Wenzel, R. M., Resistance of solid surfaces to wetting the water. Ind. Eng. Chem., 1936, 28, 988–994.

  • Cassie, A. B. D. and Baxter, S., Wettability of porous surface. Trans. Faraday Sci., 1944, 90, 546–551.

  • Barati. N., Fghihi Sani, M. A., Ghasemi, H., Sadeghian, Z. and Mirhosein, S. M. M., Preparation of uniform TiO2 nano-structure film on 316L stainless steel by sol–gel dip coating. J. Appl. Surf. Sci., 2009, 255, 828–833.

  • Young, T., An essay on the cohesion of fluids. Philos. Trans. R. Soc. London, 1805, 95, 65–87.

  • Yu, D. et al., Corrosion resistance of three-layer superhydrophobic composite coating on carbon steel in seawater. Electrochim. Acta, 2013, 97, 409–419.

  • Mohamed Adel, M. A, Abdullah, A. M. and Younan, N. A., Corrosion behavior of super-hydrophobic surfaces: a review. Proc. Arab. J. Chem., 2014; doi: 10.1016/j.arabjc.2014.03.006 16. Beckford, S., Zou, M., Micro/nano engineering on stainless steel substrates to produce superhydrophobic surface. Thin Solid Film, 2011, 520, 1520–1524.

  • Chen, L. J., Chen, M., Di Zhou, H. and Chen, J. M., Preparation of superhydrophobic surface on stainless steel. Appl. Surf. Sci., 2008, 255, 3459–3462.

  • Oliver, W. C. and Pharr, G. M., An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res., 1992, 7, 1564– 1583.

  • http://www.micromaterials.co.uk/

  • ASTM D3719-00, Standard test method for quantifying dirt collection on coated exterior panels. ASTM International, PA, USA, 2000, www.astm.org

  • ASTM G5-14, Standard reference test method for making potentiodynamic anodic polarization measurements. ASTM International, PA, USA, 2014; www.astm.org

  • ASTM NACE/ASTMG31-12a, Standard Guide for laboratory immersion corrosion testing of metals. ASTM International, PA, USA, 2012; www.astm.org

  • ASTM B117-11, Standard practice for operating salt spray (fog) apparatus. ASTM International, PA, USA, 2011; www.astm.org


Abstract Views: 411

PDF Views: 143




  • Effect of Sandblasting, Annealing and Hydrophobic Treatment on the Nano-Mechanical and Corrosion Behaviour of n-TiO2-Coated 316L Stainless Steel

Abstract Views: 411  |  PDF Views: 143

Authors

Zaki Ahmad
Department of Chemical Engineering, COMSATS Institute of Information Technology, Lahore, Pakistan
Faheemuddin Patel
King Fahd University of Petroleum and Minerals, Dhahran, Saudi Arabia
Naila Riaz Mastoi
Department of Chemical Engineering, COMSATS Institute of Information Technology, Lahore, Pakistan
Ayesha Saddiqa
Department of Chemical Engineering, COMSATS Institute of Information Technology, Lahore, Pakistan

Abstract


In this article, the effect of hydrophobic coated and uncoated surfaces on the corrosion resistance, tribological property, and surface morphology and nanomechanical properties is presented. A hierarchical surface (micro/nano) was prepared by ultra shot penning of 316L stainless steel at 20 kHz. Chemical vapour deposition technique was used for deposition of the coating, and coating thickness of 0.5 μm was obtained. A maximum hardness of 6.7 and 6.32 GPa was exhibited by the sandblasted (SB), annealed (SBAT) and coated (SBAT) samples respectively. The beneficial effect of annealing and surface roughness was clearly indicated by the sandblasted, annealed and coated specimens. They showed the highest value of reduced modulus maximum resistance to scratch tests and a high adhesion as indicated by scratch path profiles. The lowest corrosion rates were obtained by SBAT specimens (1.32 mpy) in 3.5 wt% NaCl. After application of 3.5% fluoroalkylsilane (FAS13), the corrosion rate was reduced to 0.04 mpy with no evidence of localized pitting. The water contact angle using DSA-100 system was measured to be 120° for SBAT and 80-90° for the samples.

Keywords


Annealing, Chemical Vapour Deposition, Corrosion, Sandblasting, Super Hydrophobicity.