Heat Flow Simulation and Evolution of Microstructure in Welding of Rail Steel


Affiliations
1 Department of Metallurgical & Materials Engineering, National Institute of Technology Karnataka, Surathkal, Mangalore, India
     

   Subscribe/Renew Journal


In the present study heat flow simulation was carried out to predict the microstructure and examine the effect of preheat and plate thickness on cooling rate of the weld metal. SOLIDCAST software is used for simulating thermal regime in the base metal. The results of simulation studies revealed that cooling rate and hence the evolution of microstructure along the parent metal were functions of the preheating temperature and the plate thickness. The superimposed simulated temperatures on CCT diagram indicated the absence of martensite precipitation in HAZ region and this was experimentally verified. The results also indicated the possibility of suggesting the preheating temperature for defect-free welding of plates of given thickness.


User
Subscription Login to verify subscription
Notifications
Font Size

Abstract Views: 319

PDF Views: 5




  • Heat Flow Simulation and Evolution of Microstructure in Welding of Rail Steel

Abstract Views: 319  |  PDF Views: 5

Authors

K. Biju
Department of Metallurgical & Materials Engineering, National Institute of Technology Karnataka, Surathkal, Mangalore, India

Abstract


In the present study heat flow simulation was carried out to predict the microstructure and examine the effect of preheat and plate thickness on cooling rate of the weld metal. SOLIDCAST software is used for simulating thermal regime in the base metal. The results of simulation studies revealed that cooling rate and hence the evolution of microstructure along the parent metal were functions of the preheating temperature and the plate thickness. The superimposed simulated temperatures on CCT diagram indicated the absence of martensite precipitation in HAZ region and this was experimentally verified. The results also indicated the possibility of suggesting the preheating temperature for defect-free welding of plates of given thickness.