Effects of Using of Modified Al-Mg (AA 5356) Filler on Cracking Susceptibility of Al-Mg-Si (AA 6061) Alloy Welds


Affiliations
1 Department of Metallurgical & Materials Engineering Indian Institute of Technology Madras, Chennai, India
     

   Subscribe/Renew Journal


The paper deals with an intention of solving HAZ problems through manipulating fusion zone chemistry and microstructure. Grain refiners such as Sc, Ti+B and Zr have been added to fusion zone through the AA5356 filler metal. The results indicated that the maximum refinement in the weld microstructure and consequent reduction in cracking susceptibility in alloy AA6061 can be achieved using AA5356 filler metal with 0.5% Sc addition.

Keywords

Grain Refinement, Welds, Aluminium Alloy, Partially Melted Zone, Haz Cracks, Liquation.
User
Subscription Login to verify subscription
Notifications
Font Size

Abstract Views: 263

PDF Views: 6




  • Effects of Using of Modified Al-Mg (AA 5356) Filler on Cracking Susceptibility of Al-Mg-Si (AA 6061) Alloy Welds

Abstract Views: 263  |  PDF Views: 6

Authors

K. Prasad Rao
Department of Metallurgical & Materials Engineering Indian Institute of Technology Madras, Chennai, India
N. Ramanaiah
Department of Metallurgical & Materials Engineering Indian Institute of Technology Madras, Chennai, India
B. Vamsikrishna
Department of Metallurgical & Materials Engineering Indian Institute of Technology Madras, Chennai, India

Abstract


The paper deals with an intention of solving HAZ problems through manipulating fusion zone chemistry and microstructure. Grain refiners such as Sc, Ti+B and Zr have been added to fusion zone through the AA5356 filler metal. The results indicated that the maximum refinement in the weld microstructure and consequent reduction in cracking susceptibility in alloy AA6061 can be achieved using AA5356 filler metal with 0.5% Sc addition.

Keywords


Grain Refinement, Welds, Aluminium Alloy, Partially Melted Zone, Haz Cracks, Liquation.