Influence of Specimen Temperature on Wear Characteristics of AA6063 Aluminium Alloy


Affiliations
1 Department of Mechanical Engineering, Amrita School of Engineering Coimbatore, Amrita VishwaVidyapeetham, Amrita University, Coimbatore, India
     

   Subscribe/Renew Journal


Dry sliding wear performance of aluminium alloy (AA 6063) was studied by varying applied normal load, sliding velocity and varying specimen temperatures from 50 to 150 °C. The results signify that the wear increases as the load increases from 10 to 20 N, while it decreases when the sliding velocity of the specimen increases from 1 to 2 m/s at room temperature. As the temperature of the specimen increases, the wear rate increases marginally at initial stage and then increases rapidly for a constant load and velocity. The specific wear was found to be decreased when load and sliding velocity were increased. However, in the case of varying specimen temperature condition, particularly at elevated temperature of the specimen, the specific wear showed an increasing trend. Coefficient of friction (COF) was nearly stable to both load and velocity, but it is marginally vary when temperature of the specimen increases from 50 to 100 °C and it decreases rapidly from 100 to 150 °C.

Keywords

AA 6063 Alloy, Coefficient of Friction, Pin-on-Disc, Specific Wear Rate, Wear Rate, Wear Resistance.
Subscription Login to verify subscription
User
Notifications
Font Size


  • C. S. Ramesh and Abrar Ahamed, Wear, 271, 1928 (2011).

  • N. Arun Prakash, R. Gnanamoorthy and M. Kamaraj, Wear, 294-295, 427 (2012).

  • G. Mrówka-Nowotnik, Arch. Mater. Sci. Eng., 46, 2, 98 (2010).

  • N. Arun Prakash, R. Gnanamoorthy and M. Kamaraj, Mater. Design, 31, 4066 (2010).

  • L. Karthikeyan, and V. S. Senthil Kumar, Mater. Design, 32, 3085 (2011).

  • J. P. Bourget, M. Fafardb, H. R. Shakeri and T. Côté, J. Mater. Processing Technol., 209, 5035 (2009).

  • K. Turbalioglu and Y. Sun, Sci. Res. Essays, 6, 2832 (2011).

  • I. Balasubramanian and R. Maheswaran, Mater Design, 65, 511 (2015).

  • K. K. Alanemea and A. O. Aluko, W. Indian J. Eng., 34, 80 (2012).

  • S. Aribo, J. A. Omotoyinbo, and D. O. Folorunso, Leonardo Electron J. Pract. Tech., 18, 9 (2011).

  • H. Arik, Y. Ozcatalbas and M.t Turker, Mater. Design, 27, 799 (2006).

  • L. Lei, L. Weiwei, T. Yiping, S. Bin and H. Wenbin, Wear, 266, 733 (2009).

  • K. M. Shorowordi, A. S. M .A. and Haseeb, J. P. Celis, Wear, 261, 634 (2006).

  • N. Radhika and N. Ragu, Int. J. Mater. Res., 106, 1 (2015).

  • H. G. Zhu, Y. L. Ai, J. Min, Q. Wu and H. Z. Wang, Wear, 268, 1465 (2010).

  • N. Radhika and R. Subramanian, Int. J. Mater. Res., 105, 875 (2014).

  • S. Natarajan, R. Narayanasamy, S. P. Kumaresh Babu, G. Dinesh, B. Anil Kumar and K. Sivaprasad, Mater. Design, 30, 2521 (2009).

  • M. Muratog˘lu and M. Aksoy, Mat. Sci. Eng. A, 282, 91 (2000).

  • A. Ramasundaram, S. Ilangovan, Sanjivi Arul and A. Shanmugasundaram, Int. J. Appl. Eng. Res., 10, 15417 (2015).


Abstract Views: 248

PDF Views: 2




  • Influence of Specimen Temperature on Wear Characteristics of AA6063 Aluminium Alloy

Abstract Views: 248  |  PDF Views: 2

Authors

S. Ilangovan
Department of Mechanical Engineering, Amrita School of Engineering Coimbatore, Amrita VishwaVidyapeetham, Amrita University, Coimbatore, India
A. Shanmugasundaram
Department of Mechanical Engineering, Amrita School of Engineering Coimbatore, Amrita VishwaVidyapeetham, Amrita University, Coimbatore, India
Sanjivi Arul
Department of Mechanical Engineering, Amrita School of Engineering Coimbatore, Amrita VishwaVidyapeetham, Amrita University, Coimbatore, India

Abstract


Dry sliding wear performance of aluminium alloy (AA 6063) was studied by varying applied normal load, sliding velocity and varying specimen temperatures from 50 to 150 °C. The results signify that the wear increases as the load increases from 10 to 20 N, while it decreases when the sliding velocity of the specimen increases from 1 to 2 m/s at room temperature. As the temperature of the specimen increases, the wear rate increases marginally at initial stage and then increases rapidly for a constant load and velocity. The specific wear was found to be decreased when load and sliding velocity were increased. However, in the case of varying specimen temperature condition, particularly at elevated temperature of the specimen, the specific wear showed an increasing trend. Coefficient of friction (COF) was nearly stable to both load and velocity, but it is marginally vary when temperature of the specimen increases from 50 to 100 °C and it decreases rapidly from 100 to 150 °C.

Keywords


AA 6063 Alloy, Coefficient of Friction, Pin-on-Disc, Specific Wear Rate, Wear Rate, Wear Resistance.