Friction and Adhesive Wear Study of Flame Sprayed Nickel Base Powder Coating


Affiliations
1 Department of Mechanical Engineering, School of Engineering, Gautam Buddha University, Greater Noida - 201312, Uttar Pradesh, India
2 Department Mechanical Engineering, School of Engineering, Gautam Buddha University, Greater Noida - 201312, Uttar Pradesh, India
     

   Subscribe/Renew Journal


Nickel base alloys are being widely used to improve the abrasive and adhesive wear resistance of various industrial components. In the present investigation, commercially available Ni-base (nickel-base) powder (MEC 1260) was used for coating deposition. The coating was deposited by flame spraying process. The microstructure of the flame sprayed coating mainly showed Ni-cells surrounded by eutectic. The Ni (nickel), Cr (chromium) and Fe (iron) were uniformly distributed in the coating while the distribution of boron was found along the grain boundaries. The Rockwell hardness of the coating was found as 56±8 (HRc). Sliding wear resistance of coating is 3-4 times higher than substrate.

Keywords

Adhesive Wear, Coefficient of Friction, Flame Sprayed, Hardness, Microstructure, Ni-Base.
Subscription Login to verify subscription
User
Notifications
Font Size


  • L. Prchlik, S. Sampath, J. Gutleber, G. Bancke and A.W. Ruff, Wear, 249, 1103 (2001). Crossref

  • R.C. Tucker, ‘ASM Handbook: Surface Engineering’, Vol. 5, ASM International, Materials Park, OH, 497 (1994).

  • H. Herman, ‘Thermal Spray Coatings, Metallurgical and Ceramic Protective Coatings’, Chapman & Hall, London, 261 (1996).

  • E. Fernandez, M. Cadenas, R. Gonzalez, C. Navas, R. Fernandez and J. de Damborenea, Wear, 259, 870 (2005). Crossref

  • J. M. Miguel, J. M. Guilemany and S. Vizcaino, Tribol. Int., 36, 181 (2003). Crossref

  • E. R. Novinski, Proceedings of 3rd National Thermal Spray Conference, USA, 151 (1990).

  • M. Dorfman, Proceedings of 13th International Thermal Spray Conference, USA, 587 (1992).

  • L. Jacobs, M.M. Hyland and M. De Bonte, J. Therm. Spray Technol., 8, 125 (1999). Crossref

  • L. Zhao, M. Maurer, F. Fischer, R. Dicks, and E. Lugscheider, Wear, 257, 41 (2004). Crossref

  • J. Wang, K. Li, D. Shu, X. He, B. Sun, Q. Guo, M. Nishio and H. Ogawa, Mater. Sci. Eng. Abstr., 371, 187 (2004). Crossref

  • Y. Ishikawa, J. Kawakita and S. Kuroda, Mater. Trans., 46, 1671 (2005). Crossref

  • S. Sharma, Journal of the Institution of Engineers (India) ; Series D - Metallurgical & Materials and Mining Engineering, 93, 7 (2012).

  • S. Sharma, Journal of the Institution of Engineers (India); Series D - Metallurgical & Materials and Mining Engineering, 94, 75 (2013).

  • S. Sharma, J. Therm. Spray Technol., 21, 773 (2012). Crossref

  • R. Gonzalez, M. Cadenas, R. Fernandez, J. L. Cortizo and E. Rodrıguez, Wear, 262, 301 (2007). Crossref

  • M. K. Stanford and V. K. Jain, Wear, 251, 990 (2001). Crossref

  • B. Xua, Z. Zhua, S. Maa, W. Zhang and W. Liu, Wear, 257, 1089 (2004). Crossref

  • M. Mohanty, R. W. Smith, M De Bonte, J. P. Celis and E.Lugscheider, Wear, 198, 251 (1996). Crossref

  • Y. Ishikawa, S. Kuroda, J. Kawakita, Y. Sakamoto and M. Takaya, Surf. Coat. Technol., 201, 4718 (2007). Crossref


Abstract Views: 312

PDF Views: 5




  • Friction and Adhesive Wear Study of Flame Sprayed Nickel Base Powder Coating

Abstract Views: 312  |  PDF Views: 5

Authors

Sushil Kumar
Department of Mechanical Engineering, School of Engineering, Gautam Buddha University, Greater Noida - 201312, Uttar Pradesh, India
Shashi Prakash Dwivedi
Department Mechanical Engineering, School of Engineering, Gautam Buddha University, Greater Noida - 201312, Uttar Pradesh, India
Satpal Sharma
Department Mechanical Engineering, School of Engineering, Gautam Buddha University, Greater Noida - 201312, Uttar Pradesh, India

Abstract


Nickel base alloys are being widely used to improve the abrasive and adhesive wear resistance of various industrial components. In the present investigation, commercially available Ni-base (nickel-base) powder (MEC 1260) was used for coating deposition. The coating was deposited by flame spraying process. The microstructure of the flame sprayed coating mainly showed Ni-cells surrounded by eutectic. The Ni (nickel), Cr (chromium) and Fe (iron) were uniformly distributed in the coating while the distribution of boron was found along the grain boundaries. The Rockwell hardness of the coating was found as 56±8 (HRc). Sliding wear resistance of coating is 3-4 times higher than substrate.

Keywords


Adhesive Wear, Coefficient of Friction, Flame Sprayed, Hardness, Microstructure, Ni-Base.