Enhanced Dielectric Properties of Polypropylene Based Composite Using Zinc Oxide Nanorods Filler


Affiliations
1 Department of Physics, Sathyabama University, Chennai-600119, Tamil Nadu, India
2 Center for Nanoscience and Nanotechnology, Sathyabama University, Chennai-600119, Tamil Nadu, India
     

   Subscribe/Renew Journal


Polypropylene and zinc oxide nanorods composites were prepared by combination of solution and mixture melting methods. Dielectric properties of the composite thin films were studied to see if zinc oxide nanorods have effect on the dielectric properties of polypropylene thin film. Introduction of zinc oxide nanorods at low filler content in the polypropylene matrix significantly improves the dielectric constant of the matrix. Simultaneously the structure of the composites was characterized by UV, XRD and SEM to understand the features in the structure that determine the functionality of the material. Composites with different weight percentage of zinc oxide nanorods show better absorption in the UV region compared to polypropylene matrix. This is due to the inherent capability of nano zinc oxide to absorb in the UV region. X-ray diffraction pattern of nanocomposites show sharp and highly intense peaks whereas neat polypropylene shows less intense peaks. This may due to the development of crystallinity in the polymer. Uniform distribution of zinc oxide which have a width of around 160-200 nm is observed in the SEM photographs of composites.


Keywords

Film Capacitor, Dielectric Properties, Polypropylene, Zinc Oxide Nanorods Composites.
Subscription Login to verify subscription
User
Notifications
Font Size


  • C. S. Reddy and C. K. Das, J. Appl. Polym. Sci., 102, 2117 (2006). DOI: 10. 1002/app. 24131 Crossref

  • G. Z. Papageorgiou, D. S. Achilias, D. N. Bikiaris and G. P. Karayannidis, Thermochim. Acta., 247, 117 (2005). DOI:10.1016/j.tca.2004 09.001. Crossref

  • O. H. Lin, H. M. Akil and Z. A. M. Ishak, Polym. Compo., 30: 1693 (2009). DOI:10.1002/pc.20744. Crossref

  • P. B. Leng, H. M. Akil and O. H. Lin, J. Compos. Sci. Tech. 26, 761 (2007). DOI:10.1016/j.compscitech.2012.01.001 Crossref

  • O. H. Lin, Z. A. M. Ishak and H. M. Akil, Mater. Des., 30(3), 748 (2009). DOI:10.1016/j.matdes.2008.05.007. Crossref

  • J. Jordan, K. I. Jacob, R. Tannenbaum, M. A. Sharaf and I. Jasiuk, Mater. Sci. Eng., 393, 1(2005). DOI: 10.1016/j. msea.2004.09.044. Crossref

  • M. Avella, F. Bondioli, C. Valeria, E. Di Pace, M. E. Errico, A. M. Ferrari , B. Focher and M. Malinconico, Compos. Sci. Tech., 66, 886 (2006). DOI:10.1016/j.compscitech.2005.08.014. Crossref

  • J. Vera-Agullo, G. Gloria-Pereira, H. Varela-Rizo, G. L. Jose and I. Martin-Gullon, Compos. Sci. Tech., 69, 1521 (2009). DOI: 10.1016/j.compscitech.2008.11.032 Crossref

  • B. Ha-da, G Zhao-xia and Y Jian, Chin. J. Polymer. Sci., 27, 393 (2009). DOI:10.1142/S0256767909004059. Crossref

  • X. Hesheng, W. Qi, L. Kanshe and H. Guo-Hua, J. Appl. Polymer. Sci., 93, 378 (2004). DOI:10.1002/app.20435. Crossref

  • K. Prashantha, J. Soulestin, M. F. Lacrampe, M. Claes, G. Dupin and P. Krawczak, eXPRESS Poly. Letters, 2, 735 (2008). DOI:10.3144/expresspolymlett.2008.87. Crossref

  • Y. Tang, Y. Hu, L. Song, R. Zong, Z. Gui, Z. Chen and W. Fan. Polymer. Degrad. Stabil., 82, 127 (2003). DOI:10.1016/S0141-3910(03)00173-3 Crossref

  • P. Maiti, P. H. Nam, M. Okamoto, N. Hasegawa and A. Usuki, Macromolecules, 35, 2042 (2002). DOI:10.1021/ma010852z. Crossref

  • Y. Dang, Y. Wang, Y. Deng, M. LI, Y. Zhang and Zhiweizhang, Progr. Nat. Sci., 21, 216 (2011). DOI:10. 1016/S1002-0071(12)60033-1. Crossref

  • J. C. Johnson, H. Yan, R. D. Schaller, L. H. Haber, R. J. Saykally and P. Yang, J. Phys. Chem., 105, 11387 (2001). DOI:10.1021/jp012304t. Crossref

  • H. Rensmo, K. Keis, H. Lindstrom, S. Sodergren, A. Solbrand, A. Hagfeldt, and S. E. Lindquist, J. Phys. Chem. B, 101, 2598 (1997). DOI:10.1021/jp962918b. Crossref

  • S. Mahmud, M. J. Abdullah, G. A. Putrus, J. Chong and A. K. Mohamad, Synth. React. Inorg. Met. Org. Chem., 36, 155 (2006). DOI:10.1080%2F15533170500524462.

  • A. Becheri, M. Dürr, P. L. Nostro and P. Baglioni, Journal of Nanoparticle Research 10, 679 (2008). DOI:10.1007/s11051-007-9318-3. Crossref

  • Y. W. Heo, L. C. Tien and D. P. Norton, Appl. Phys. Lett., 85, 11 (2004). DOI:10.1063/1.1792373. Crossref

  • B. D. Cullity, Elements of X-ray diffraction, AddissonWesley, 2nd edition, (1978).

  • N. Kiomarsipour and R. S. Razavi, Superlattice. Microst., 52, 704 (2012). DOI:10.1016/j.spmi.2012.07.003. Crossref

  • Z. L. Wang, Mater. Today, 7, 26 (2004). DOI:10.1016/S13697021(04)00286-X. Crossref

  • A. Umar, S. H. Kim, E. K. Sun and Y. B. Hahn, Chem. Phys. Lett., 440, 110 (2007). DOI:10.1016/j.cplett.2007.04.006. Crossref

  • O. H. Lin, H. MdAkil, and S. Mahmud, Adv. Compos. Lett., 18, 83 (2009). DOI:http://www.acletters.org/pdf/18-3-2.pdf

  • R. Wahab, S. G. Ansari, Y. S. Kim, M. A. Dar, H. S. Shin, J. Alloy. Comp., 461, 66 (2008). DOI:10.1016/j.jallcom.2007.07.029. Crossref

  • G. Mani, Q. Fan, C. U. Samuel, Y. Yang, J. of Appl. Poly. Science, 97, 218 (2005). DOI:10.1002/app.21750. Crossref

  • Z. M. Dang, L. Wang and Y. Yin, Adv. Mater., 19, 852 (2007). DOI:10.1002/adma.200600703. Crossref


Abstract Views: 311

PDF Views: 3




  • Enhanced Dielectric Properties of Polypropylene Based Composite Using Zinc Oxide Nanorods Filler

Abstract Views: 311  |  PDF Views: 3

Authors

D. J. Sharmila
Department of Physics, Sathyabama University, Chennai-600119, Tamil Nadu, India
J. Brijitta
Center for Nanoscience and Nanotechnology, Sathyabama University, Chennai-600119, Tamil Nadu, India
R. Sampathkumar
Department of Physics, Sathyabama University, Chennai-600119, Tamil Nadu, India

Abstract


Polypropylene and zinc oxide nanorods composites were prepared by combination of solution and mixture melting methods. Dielectric properties of the composite thin films were studied to see if zinc oxide nanorods have effect on the dielectric properties of polypropylene thin film. Introduction of zinc oxide nanorods at low filler content in the polypropylene matrix significantly improves the dielectric constant of the matrix. Simultaneously the structure of the composites was characterized by UV, XRD and SEM to understand the features in the structure that determine the functionality of the material. Composites with different weight percentage of zinc oxide nanorods show better absorption in the UV region compared to polypropylene matrix. This is due to the inherent capability of nano zinc oxide to absorb in the UV region. X-ray diffraction pattern of nanocomposites show sharp and highly intense peaks whereas neat polypropylene shows less intense peaks. This may due to the development of crystallinity in the polymer. Uniform distribution of zinc oxide which have a width of around 160-200 nm is observed in the SEM photographs of composites.


Keywords


Film Capacitor, Dielectric Properties, Polypropylene, Zinc Oxide Nanorods Composites.