Experimental investigation of additive manufacturing of SS 316L using laser direct metal deposition


Affiliations
1 Indian Institute of Technology Madras, Chennai, India
     

   Subscribe/Renew Journal


Laser direct metal deposition (LDMD) is a rapidly emerging additive manufacturing technique offering attractive characteristics like high deposition rates, component repair, and deposition of functionally graded materials. Experimental investigations have been carried out to deposit SS 316L structures at higher deposition rates using LDMD. A continuous fiber laser operating at a wavelength of 1070 nm is used to deposit the structures under different processing parameters like power, scanning speed, and powder feed rate. A power range of 600 W to 1200 W is found to be optimal with speed varying in the range between 10 mm/sec and 25 mm/sec. At low power with higher velocities, a low layer thickness is obtained and vice-versa. With an increase in the power and the decrease in the speed, deposition rates are increased. The findings will help to develop pre-processing, online-processing, and post-processing strategies for LDMD.

Keywords

Laser Direct Metal Deposition, SS 316 L, Deposition Rate, Additive Manufacturing.
User
Subscription Login to verify subscription
Notifications
Font Size

  • Costa, L., Vilar, R.(2009). Laser powder deposition. Rapid Prototyping Journal, 15(4), 264-279.

  • Jinoop, A. N., Paul, C. P., & Bindra, K. S. (2019). Laser-assisted directed energy deposition of nickel super alloys: a review. Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications, 233(11). 2376-2400.

  • Sames, W. J., List, F. A., Pannala, S., Dehoff, R. R., & Babu, S. S. (2016). The metallurgy and processing science of metal additive manufacturing. International Materials Reviews, 61(5), 315-360.

  • Sasikumar, R., Kannan, A. R., Kumar, S. M., Pramod, R., Kumar, N. P., Shanmugam, N. S., & Sivankalai, S. (2022). Wire arc additive manufacturing of functionally graded material with SS 316L and IN625: Microstructural and mechanical perspectives. CIRP Journal of Manufacturing Science and Technology, 38, 230-242.

  • Steen, W. M. (2003). Rapid Prototyping and Low-volume Manufacture. In: Laser Material Processing, (279-299). Springer- London.

  • Svetlizky, D., Das, M., Zheng, B., Vyatskikh, A. L., Bose, S., Bandyopadhyay, A., Schoenung, J. M., Lavernia, E. J., Eliaz, N. (2021). Directed energy deposition (DED) additive manufacturing: Physical characteristics, defects, challenges and applications. Materials Today, 49, 271-295.

  • Syed, W. U. H., Pinkerton, A. J., & Li, L. (2005). A comparative study of wire feeding and powder feeding in direct diode laser deposition for rapid prototyping. Applied Surface Science, 247(1-4), 268-276. Takemura, S., Koike, R., Kakinuma, Y., Sato, Y., & Oda, Y. (2019). Design of powder nozzle for high resource efficiency in directed energy deposition based on computational fluid dynamics simulation. International Journal of Advanced Manufacturing Technology, 105(10), 4107-4121.

  • Zadi-Maad, A., Rohib, R., & Irawan, A. (2018). Additive manufacturing for steels: A review. In IOP Conference Series: Materials Science and Engineering, 285(1), 012028.


Abstract Views: 102

PDF Views: 0




  • Experimental investigation of additive manufacturing of SS 316L using laser direct metal deposition

Abstract Views: 102  |  PDF Views: 0

Authors

Satyanarayana Rao Gogineni
Indian Institute of Technology Madras, Chennai, India
Sanasam Sunderlal Singh
Indian Institute of Technology Madras, Chennai, India
G. L. Samuel
Indian Institute of Technology Madras, Chennai, India

Abstract


Laser direct metal deposition (LDMD) is a rapidly emerging additive manufacturing technique offering attractive characteristics like high deposition rates, component repair, and deposition of functionally graded materials. Experimental investigations have been carried out to deposit SS 316L structures at higher deposition rates using LDMD. A continuous fiber laser operating at a wavelength of 1070 nm is used to deposit the structures under different processing parameters like power, scanning speed, and powder feed rate. A power range of 600 W to 1200 W is found to be optimal with speed varying in the range between 10 mm/sec and 25 mm/sec. At low power with higher velocities, a low layer thickness is obtained and vice-versa. With an increase in the power and the decrease in the speed, deposition rates are increased. The findings will help to develop pre-processing, online-processing, and post-processing strategies for LDMD.