A Simple Sonication-assisted Exfoliation and Characterization of Few Layered Graphene Nanosheets


Affiliations
1 Centre for Nanoscience and Applied Thermodynamics, Department of Physics, St. Joseph's College, Trichy-620002, India
 

Reduced graphene oxide (rGO) is a radical candidate for energy related sector. In this paper, we report how few layers graphene that can be produced in large quantity with low defect ratio from exfoliation of GO by using a sonication energy. GO was prepared from graphite powder by modified Hummer's method. GO then further exfoliated to graphene oxide by using ultrasonic irradiation.The ultrasonication approach for the exfoliation of rGO nanosheet is relatively fast, cost-effective and efficient as compared to other methods.The characterization techniques such as UV and FT-IR analysis confirmed the reduction of GO to rGO. The structure and morphology of as-prepared rGO nanosheet were studied using a range of techniques such as XRD, Raman spectroscopy, SEM, and TEM.The experimental results suggest that the graphene sheets obtained by this simple exfoliation method after the heat reduction had an excellent exfoliation into a few layered graphene sheets.

Keywords

Ultrasonication, rGO, XRD, Electron Microscopy.
User
Notifications
Font Size

  • Can W., Liang Z., Qiao W-m and Ling L-c. Preparation of graphene nanosheets through detonation, New Carbon Mat. 26 (2011) 21-25.

  • Sun J., Liu H., Chen X., Evans D.G., Yang W. and Duan X., Synthesis of graphene nanosheets with good control over the number of layers within the two-dimensional galleries of layered double hydroxides, Chem. Commun. 48 (2012) 8126-8128.

  • Wang G., Yang J., Park J., Gou X., Wang B., Liu H. et al. Facile synthesis and characterization of graphene nanosheets, J. Phys. Chem. 112 (2008) 8192-8195.

  • Yu H., Zhang B., Bulin C., Li R. and Xing R., Highefficient synthesis of graphene oxide based on improved Hummers method, Sci. Rep. 6 (2016) 36143.

  • Minitha C.R. and Rajendrakumar R.T., Synthesis and characterization of reduced grapheneoxide. Adv. Mat. Res. 678 (2013) 56-60.

  • Badiei E., Sangpour P., Bagheri M. and Pazouki M., Graphene oxide antibacterial sheets: Synthesis and characterization (research note), IJE Transactions C: Aspects 27 (2014) 1803-1808.

  • Stankovich S., Dikin D.A., Piner R.D., Kohlhaas K.A., Kleinhammes A., Jia Y. et al., Synthesis of graphenebased nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45 (2007)1558-1565.

  • Raccichini R., Varzi A., Passerini S. and Scrosati B., The role of graphene for electrochemical energy storage. Nature Mat. 14 (2015) 271-279.

  • Movahed S.K., Fakharian M., Dabiri M. and Bazgir A., Gold nanoparticles decorated reduced graphene oxide sheets with significantly high catalytic activity for ullmann homocoupling, RSC Adv. 4 (2014) 5243-5247.

  • Nethravathi C. and Rajamathi M., Chemically modified graphene sheets produced by the solvothermal reduction of colloidal dispersions of graphite oxide. Carbon 46 (2008) 1994-1998.


Abstract Views: 361

PDF Views: 0




  • A Simple Sonication-assisted Exfoliation and Characterization of Few Layered Graphene Nanosheets

Abstract Views: 361  |  PDF Views: 0

Authors

Rintu Varghese
Centre for Nanoscience and Applied Thermodynamics, Department of Physics, St. Joseph's College, Trichy-620002, India
H. Joy Prabu
Centre for Nanoscience and Applied Thermodynamics, Department of Physics, St. Joseph's College, Trichy-620002, India
I. Johnson
Centre for Nanoscience and Applied Thermodynamics, Department of Physics, St. Joseph's College, Trichy-620002, India

Abstract


Reduced graphene oxide (rGO) is a radical candidate for energy related sector. In this paper, we report how few layers graphene that can be produced in large quantity with low defect ratio from exfoliation of GO by using a sonication energy. GO was prepared from graphite powder by modified Hummer's method. GO then further exfoliated to graphene oxide by using ultrasonic irradiation.The ultrasonication approach for the exfoliation of rGO nanosheet is relatively fast, cost-effective and efficient as compared to other methods.The characterization techniques such as UV and FT-IR analysis confirmed the reduction of GO to rGO. The structure and morphology of as-prepared rGO nanosheet were studied using a range of techniques such as XRD, Raman spectroscopy, SEM, and TEM.The experimental results suggest that the graphene sheets obtained by this simple exfoliation method after the heat reduction had an excellent exfoliation into a few layered graphene sheets.

Keywords


Ultrasonication, rGO, XRD, Electron Microscopy.

References