Elastic Behavior and Internal Friction Loss of NiMgCuZn Ferrospinels for Microinductor Applications


Affiliations
1 Ceramic Composite Materials Laboratory, Department of Physics, Sri Krishnadevaraya University, Ananthapur - 505 003, India
2 Department of Physics, Indian Institute of Technology, Chennai - 600 036, India
 

Two series of NiMgCuZn ferrites namely 1) NixMg0.6xZn0.3Fe2O4 with x=0.0,0.1,0.2,0.3; 2)Ni0.35Mg0.2yCu0.05Zn0.5-yFe2O4 with y=0.0,0.1,0.2 were prepared by conventional double sintering process with a view to examine their use as core materials for microinductor applications. The x-ray analysis revealed the single phase formation. In order to examine their elastic behaviour, the temperature variation of longitudinal modulus and acoustic loss (Q-1) of these samples at 142 kHz were studied in temperature range 300 to 630 K using composite resonator technique. The longitudinal modulus showed an abrupt break near curie temperature transition in all the samples studied in the present work. The temperature variation of internal friction loss (Q-1) showed a corresponding stress induced relaxation peak at this phase transition. The results are explained in the light of structural phase transition.
User
Notifications
Font Size

Abstract Views: 218

PDF Views: 0




  • Elastic Behavior and Internal Friction Loss of NiMgCuZn Ferrospinels for Microinductor Applications

Abstract Views: 218  |  PDF Views: 0

Authors

N. Varalaxmi
Ceramic Composite Materials Laboratory, Department of Physics, Sri Krishnadevaraya University, Ananthapur - 505 003, India
M. Venkata Ramana
Ceramic Composite Materials Laboratory, Department of Physics, Sri Krishnadevaraya University, Ananthapur - 505 003, India
N. Ramamanohar Reddy
Ceramic Composite Materials Laboratory, Department of Physics, Sri Krishnadevaraya University, Ananthapur - 505 003, India
K. V. Sivakumar
Ceramic Composite Materials Laboratory, Department of Physics, Sri Krishnadevaraya University, Ananthapur - 505 003, India
E. Rajagopal
Ceramic Composite Materials Laboratory, Department of Physics, Sri Krishnadevaraya University, Ananthapur - 505 003, India
V. R. K. Murthy
Department of Physics, Indian Institute of Technology, Chennai - 600 036, India

Abstract


Two series of NiMgCuZn ferrites namely 1) NixMg0.6xZn0.3Fe2O4 with x=0.0,0.1,0.2,0.3; 2)Ni0.35Mg0.2yCu0.05Zn0.5-yFe2O4 with y=0.0,0.1,0.2 were prepared by conventional double sintering process with a view to examine their use as core materials for microinductor applications. The x-ray analysis revealed the single phase formation. In order to examine their elastic behaviour, the temperature variation of longitudinal modulus and acoustic loss (Q-1) of these samples at 142 kHz were studied in temperature range 300 to 630 K using composite resonator technique. The longitudinal modulus showed an abrupt break near curie temperature transition in all the samples studied in the present work. The temperature variation of internal friction loss (Q-1) showed a corresponding stress induced relaxation peak at this phase transition. The results are explained in the light of structural phase transition.