Bioactivity of Gutta flow II versus Modified Gutta Percha based Silicon Endodontic Sealers by Nanobioactive Fillers


Affiliations
1 Misan University/ College of Dentistry- Dept. of Oral Diagnosis, Iraq
2 Baghdad University/ College of Dentistry- Dept. of Restorative and Esthetic Dentistry, Iraq
     

   Subscribe/Renew Journal


The success of endodontic therapy is relied on radicular system cleaning, shaping, elimination of micro-organisms, and three dimensional filling of the radicular complex.This study was conducted to develop and assess new ischolar_main canal sealer incorporating nano-sized bioactive glass into Gutta Flow II. The following concentration was used depend on a pilot study included adding (3%) of 45S5 bioactive glass into the Gutta Flow II. These materials were tested through assessment bioactivity. bioactivity test was undertaken after immersion of the tested samples into PBS for three days, seven days, fourteen days, and twenty eight days using FTIR too. study was found that it’s peaks was appear at level 800-1000 cm-1. The results showed that GFII group revealed no peak at the 910 cm-1, while, while BG3% revealed 179.85 pixel height, in conclusion the newly developed sealers exhibited apparent apatite and apatite precursor forming ability significantly with BG 3% while GuttaFlow II sealer showed no apatite layer forming ability.

Keywords

Bioactivity, chemical analysis, 45S5 bioactive glass
Subscription Login to verify subscription
User
Notifications
Font Size


Abstract Views: 430

PDF Views: 0




  • Bioactivity of Gutta flow II versus Modified Gutta Percha based Silicon Endodontic Sealers by Nanobioactive Fillers

Abstract Views: 430  |  PDF Views: 0

Authors

Saad A. Ramadhan
Misan University/ College of Dentistry- Dept. of Oral Diagnosis, Iraq
Raghad A. Al hashimi
Baghdad University/ College of Dentistry- Dept. of Restorative and Esthetic Dentistry, Iraq

Abstract


The success of endodontic therapy is relied on radicular system cleaning, shaping, elimination of micro-organisms, and three dimensional filling of the radicular complex.This study was conducted to develop and assess new ischolar_main canal sealer incorporating nano-sized bioactive glass into Gutta Flow II. The following concentration was used depend on a pilot study included adding (3%) of 45S5 bioactive glass into the Gutta Flow II. These materials were tested through assessment bioactivity. bioactivity test was undertaken after immersion of the tested samples into PBS for three days, seven days, fourteen days, and twenty eight days using FTIR too. study was found that it’s peaks was appear at level 800-1000 cm-1. The results showed that GFII group revealed no peak at the 910 cm-1, while, while BG3% revealed 179.85 pixel height, in conclusion the newly developed sealers exhibited apparent apatite and apatite precursor forming ability significantly with BG 3% while GuttaFlow II sealer showed no apatite layer forming ability.

Keywords


Bioactivity, chemical analysis, 45S5 bioactive glass



DOI: https://doi.org/10.37506/v14%2Fi1%2F2020%2Fijfmt%2F193031