Development of Dissolvable Dye Transfer Inhibitor for Household Laundry


Affiliations
1 Department of Fashion Technology, PSG College of Technology, Coimbatore 641 004, India
 

This research is focused on developing a dissolvable composite polymeric film loaded with a dye transfer inhibitor. Pyridine N-oxide (PNO) is one of the amine-based dye transfer inhibitor(DTI) polymers with higher dye inhibition ability. A transparent and water-soluble PNO-loaded polymeric composite film of polyvinyl alcohol (PVA-PNO film) has been developed using the solution casting method, and the process parameters are optimised. The performance of the developed polymeric composite film has been evaluated in terms of dissolving time and dye-transfer inhibition in the laundry. The results indicate that the addition of the cross-linking agent increases the dissolving time of the film, while the addition of the plasticizer reduces it. An average of 8.5min is observed as the dissolving time for the developed product in the presence of detergent. In the laundry process, a colour difference value (ΔE) of 4.763 is noted against Reactive Blue 4 (C23H14Cl2N6O8S), and the performance of the product against multiple dyes is found to be satisfactory. The tensile strength of the film is found as 17.1 Mpa, elongation 113%, and folding endurance 250 times, confirming the better-handling property of the developed film.

Keywords

Colour Difference Value, Dissolving Time, Dye Transfer Inhibitor Polymer, Pyridine N-Oxide Film, Polyvinyl Alcohol Film.
User
Notifications
Font Size

  • Donoghue Donoghue S J & Schamp K M A, U S Pat005849684A (1998).

  • Johnson K A, Buskirk G V & Gillette S M, U S Pat005698476A(1997).

  • Voelkel T, Guckenbiehl B & Roeleke C, U S Pat0029898 A1 (2009).

  • Trinh T, Sung S L, Tordil H B & Wendland P A,U S Pat 5,767,062A(1998).

  • Srinivas B, Shih J S & Hornby J C, U S Pat 5869442A(1999)

  • Shih J S, Srinivas B & Hornby J C, U S Pat 5776879A(1998).

  • Trinh T, Sung S L, Tordil H B & Wendland P A, U S Pat 5804219A(1998).

  • Coe G, Lee F, Trinh T, Sung S L, Tordil H B & Wendl P A,U S Pat 4065257A (1972).

  • Thoen C A J K, Fredj A & Johnston J P, U S Pat 5445651A(1995).

  • Donoghue S J & Schamp K M A, U S Pat 5849684A(1995).

  • Ziskind S, U S Pat 5881412A(1999).

  • Felstead P S & Ziskind S, U S Pat 6035473A(2000).

  • Panandiker R K, Aouad Y G, Randall S L & Wertz W C, U S Pat 6833336B2(2004).

  • Felstead P S & Ziskind S, Eur Pat 1115936B1(1999).

  • Mcnamee P, Guerlédan L L & Toms D, WO 2012107405A1(2012).

  • Aouad Y G, Gordon G C, Panandiker R K & Vetter N D, Eur Pat1325106B1(2001).

  • Wattiez D & Hennion J C, U S Pat 4494264A(1985).

  • Felstead P S & Ziskind S, WO1999063142A1(1999).

  • Panandiker R, Aouad Y, Gordon G & Vetter N, U S Pat 0019564A1(2006)

  • Panandiker R, Aouad Y, Gordon G & Vetter N, U S Pat 0119721A1(2002).

  • Orlandi V, Agostini A, Orlandini F M, Curi P & Meregalli R, U S Pat8075635B2(2006).

  • Tubbs R K, J Polym Sci, 4(1966) 623.

  • Tacx J C J F, Schoffeleers H M, Brands A G M & Teuwen L, Polymer,41 (2000) 947.

  • Modi T W, Handbook of Water-Soluble Gums and Resins, edited by R L Davidson (MaGraw-Hill Book Co.), 1980, 20.

  • Lim L Y & Wan L S C, Drug Dev Ind Pharm, 20(6)(1994) 1007.

  • Rathinamoorthy R, Fibers Polym, 20(6) (2019) 1218.

  • Fujiwara N, Hikasa S & Isozaki T, U S Pat 6,956,070 B2(2005).

  • Sonenstein G G, U S Pat 4,481,326(1984).

  • Hernandez P M, Salgado S R & Saxena R, U S Pat 8,778,862 B2(2014).

  • Smith W L, Kaufmann E J& Sudbury B A, U S Pat 4,801,636 (1989).

  • Wanga S, Rena L, Lia W, Suna R& Liua S, Carbohyd Polym,103 (2014) 94.

  • Birck C, Degoutin S, TabaryN, Miri V & Bacquet M., Express Polym Lett, 8(12) (2014) 941.

  • Rathianmoorthy R, Ayswarriya N, Kadambari R, Sreelatha R & Janani K G, Indian J Fibre Text Res, 41(4)(2016) 432.

  • Hima Bindu T V L, Vidyavathi M, Kavitha K, Sastry T P & Suresh Kumar R V, Trends Biomater Artif Organs, 24(3) (2010) 123.

  • Yang C Q & Wang X, Text Res J, 66(9) (1996) 595.

  • Yang J, Webb A & Ameer G, Adv Mater, 16(2004) 511.

  • Krumova M, López D, Benavente R, Mijangos C & Pereña J M, Polymer, 41 (2000)9265.

  • Thiebaud S, Aburto J, Alric I, Borredon E, Bikiaris D, Prinos J& Panayiotou C, J Appl Polym Sci, 65(4) (1997) 705.

  • Merck J Z, Raota C S, Duarte J, Baldasso C, Crespo J da S & Giovanela M, Revista Eletrônica Em Gestão, Educação E Tecnologia Ambiental, 24 (2020) e5.

  • Sridach W, Jonjankiat S & Wittaya T, J Adhes Sci Technol,27(15) (2013) 1727.

  • Shi R, Bi J, Zhang Z, Zhu A, Chen D, Zhou X, Zhang L & Tian W, Carbohyd Polym, 74 (2008) 763.

  • Barreto P L M, Pires A T N & Soldi V, Polym Degrad Stab, 79 (2003) 147.

  • Cheng L H, Karim A A & Seow C C, J Food Sci, 71(2006) 62.

  • Sothornvit R & Krochta J M, J Food Eng, 50(3) (2001) 149.

  • Sreekumar P A, Al-Harthi M A & De S K, J Appl Polym Sci, 123 (2012) 135.

  • Zhang Y, Wright R E, Wolk D R, Tuman S J, Porbeni F E, Liu J J, Jing N & Endler E E, WO2009005884A1(2009).

  • Flores-Arriaga J C, Chavarría-Bolaños D, Pozos-Guillén A J, Escobar-Barrios V A & Cerda-Cristerna B I, J Mater Sci: Mater Med, 32 (2021) 56.

  • Rivera-Hernández G, Antunes-Ricardo M, Martínez-Morales P& Sánchezc M L, Int J Pharm, 600 (2021) 120478.

  • Amin M N & Blackburn R S, ACS Sustain Chem Eng, 3(4) (2015) 725.

  • Carrion F J, J Text Inst, 105(2) (2014) 150.


Abstract Views: 145

PDF Views: 102




  • Development of Dissolvable Dye Transfer Inhibitor for Household Laundry

Abstract Views: 145  |  PDF Views: 102

Authors

R Rathinamoorthy
Department of Fashion Technology, PSG College of Technology, Coimbatore 641 004, India

Abstract


This research is focused on developing a dissolvable composite polymeric film loaded with a dye transfer inhibitor. Pyridine N-oxide (PNO) is one of the amine-based dye transfer inhibitor(DTI) polymers with higher dye inhibition ability. A transparent and water-soluble PNO-loaded polymeric composite film of polyvinyl alcohol (PVA-PNO film) has been developed using the solution casting method, and the process parameters are optimised. The performance of the developed polymeric composite film has been evaluated in terms of dissolving time and dye-transfer inhibition in the laundry. The results indicate that the addition of the cross-linking agent increases the dissolving time of the film, while the addition of the plasticizer reduces it. An average of 8.5min is observed as the dissolving time for the developed product in the presence of detergent. In the laundry process, a colour difference value (ΔE) of 4.763 is noted against Reactive Blue 4 (C23H14Cl2N6O8S), and the performance of the product against multiple dyes is found to be satisfactory. The tensile strength of the film is found as 17.1 Mpa, elongation 113%, and folding endurance 250 times, confirming the better-handling property of the developed film.

Keywords


Colour Difference Value, Dissolving Time, Dye Transfer Inhibitor Polymer, Pyridine N-Oxide Film, Polyvinyl Alcohol Film.

References