Studying the Influence of Nano ZnO and Nano ZrO2 Additives on Properties of PMMA Denture Base


Affiliations
1 Department of Applied Sciences, Materials Science Branch, University of Technology
2 Dr. College of Dentistry, Department of Basic Sciences, Baghdad University, Iraq
3 Department of Applied Sciences, Materials Science branch, University of Technology, Baghdad, Iraq
     

   Subscribe/Renew Journal


The aim of this study was to prepare materials that use to manufacture a denture by using a composite material, also studying their properties. Poly methyl methacrylate (PMMA) resin is widely utilized in dental applications. Two types of additives (Nano zinc oxide and Nano zirconium oxide) with different weight percentages (1%, 2%, 3%, 4% and 5%) were added to PMMA resin to improve its properties. The mixture was chosen experimentally to obtain the optimum properties also to avoid cracks formation. The ratio of PMMA and dichloromethane were (20% wt) and (80% wt) respectively for pure specimens. The result showed that there was an increasing in thermal conductivity, completion strength and a decreasing in roughness.

Keywords

PMMA, Biomaterial Dental Materials, Prosthetic Dentistry.
Subscription Login to verify subscription
User
Notifications
Font Size


Abstract Views: 570

PDF Views: 0




  • Studying the Influence of Nano ZnO and Nano ZrO2 Additives on Properties of PMMA Denture Base

Abstract Views: 570  |  PDF Views: 0

Authors

Suroor Abd Alwahab
Department of Applied Sciences, Materials Science Branch, University of Technology
Jaafar M. Moosa
Dr. College of Dentistry, Department of Basic Sciences, Baghdad University, Iraq
Sadeer Muafaq
Department of Applied Sciences, Materials Science branch, University of Technology, Baghdad, Iraq

Abstract


The aim of this study was to prepare materials that use to manufacture a denture by using a composite material, also studying their properties. Poly methyl methacrylate (PMMA) resin is widely utilized in dental applications. Two types of additives (Nano zinc oxide and Nano zirconium oxide) with different weight percentages (1%, 2%, 3%, 4% and 5%) were added to PMMA resin to improve its properties. The mixture was chosen experimentally to obtain the optimum properties also to avoid cracks formation. The ratio of PMMA and dichloromethane were (20% wt) and (80% wt) respectively for pure specimens. The result showed that there was an increasing in thermal conductivity, completion strength and a decreasing in roughness.

Keywords


PMMA, Biomaterial Dental Materials, Prosthetic Dentistry.