Piezoelectric Properties of Ta (≤ 5 (mole)%) Doped in Na0.685K0.315NbO3


Affiliations
1 Department of Physics, University Science Instrumentation Centre, HNB Garhwal University, Srinagar (Garhwal)-246 174, India

To explore the piezoelectric potential of Ta doping on the MPB- like composition Na0.685K0.315NbO3, ceramic pellets of Na0.685K0.315Nb1-yTayO3 (y ≤ 0.05) were arranged by solid-state reaction method. For piezoelectric measurements, sintered pellets were electroded, in parallel capacitor configuration, with silver coating deposited by direct current (dc) magnetron sputtering of a silver target. Polarization and piezoelectric parameters were measured using a ferroelectric (PE- loop tracer) and piezo- meter (AixACCT Systems, GmbH). Composition (y) variation of remnant polarization, coercive field, converse piezoelectric coefficient (d*33), and polarization current measurements were carried out in the prepared compositions. The remnant polarization (Pr) is 18.439 μC/cm2 with a coercive field (Ec) of 8 kV/cm for NKNT single crystals. d*33 was observed 300.76 pm/V for y = 0.04 at the applied field of 22kV/cm.
User
Notifications
Font Size

Abstract Views: 152




  • Piezoelectric Properties of Ta (≤ 5 (mole)%) Doped in Na0.685K0.315NbO3

Abstract Views: 152  | 

Authors

Jyotsana Negi
Department of Physics, University Science Instrumentation Centre, HNB Garhwal University, Srinagar (Garhwal)-246 174, India
Don Biswas
Department of Physics, University Science Instrumentation Centre, HNB Garhwal University, Srinagar (Garhwal)-246 174, India
N S Panwar
Department of Physics, University Science Instrumentation Centre, HNB Garhwal University, Srinagar (Garhwal)-246 174, India

Abstract


To explore the piezoelectric potential of Ta doping on the MPB- like composition Na0.685K0.315NbO3, ceramic pellets of Na0.685K0.315Nb1-yTayO3 (y ≤ 0.05) were arranged by solid-state reaction method. For piezoelectric measurements, sintered pellets were electroded, in parallel capacitor configuration, with silver coating deposited by direct current (dc) magnetron sputtering of a silver target. Polarization and piezoelectric parameters were measured using a ferroelectric (PE- loop tracer) and piezo- meter (AixACCT Systems, GmbH). Composition (y) variation of remnant polarization, coercive field, converse piezoelectric coefficient (d*33), and polarization current measurements were carried out in the prepared compositions. The remnant polarization (Pr) is 18.439 μC/cm2 with a coercive field (Ec) of 8 kV/cm for NKNT single crystals. d*33 was observed 300.76 pm/V for y = 0.04 at the applied field of 22kV/cm.